Development and Characterization of Metal-Doped Modified CO Oxidation Catalyst for Coalbed Methane with Strong Adsorption and Water Resistance

A metal-doped modified CO oxidation catalyst with strong adsorption and water resistance for coalbed methane was prepared by the CO precipitation method. The CO ablation characteristics were tested, and the Cu Mn catalyst synthesized by metal Ce doping achieved an instantaneous ablation efficiency of 80% when in contact with CO at room temperature. By analyzing the surface crystal structure and pore characteristics, as well as by testing the ablation properties, it was found that the CO oxidation catalyst synthesized by Ce had the best effect at a precipitation temperature of 70 °C. A water-resistant CO oxidation catalyst was synthesized by adding polyvinyl alcohol (PVA) and polyvinylpyrrolidone (PVP). After storage at a relative humidity of 90%, it still had a CO adsorption rate of about 85%. The water-resistant CO oxidation catalyst prepared with polyvinyl alcohol (PVA) as an additive had a higher content of CeO2crystal nuclei, and the PVA-added CO oxidation catalyst had the best ablation characteristics. In the evaluation of the water-resistant steam ablation process, the CuMnOx-Ce-PVA catalyst showed a significant increase in intermediate products during the stress process under water vapor conditions and a decrease in the peak value of the catalyst’s binding to water, and the catalyst has a particular inhibitory influence on the adsorption of water molecules on its surface. Due to its outstanding water resistance, the catalyst was able to retain good ablation characteristics.