摘要
A single-pot surfactant-free sol-gel method is reported for the facile and bulk synthesis of ultrafine-nanospherical CeO 2 /TiO 2 composites with different CeO 2 loadings and their photocatalytic-activity for the degradation and mineralization of tetracycline (TC) under visible-light irradiation is investigated for the first time. The incorporation of CeO 2 favored the controlled crystalline growth of TiO 2 in its anatase phase, and their crystallinity and particle size were significantly decreased. The textural and optical properties of TiO 2 were also improved with the incremental addition of CeO 2 by increasing their specific surface-area and visible-light absorption respectively. The optical band gap of TiO 2 decreased to 2.24 eV with the incorporation of 1% CeO 2 and it further decreased to 2.21 eV with the incremental amount of CeO 2 . Due to the formation of heterojunction in the composite, the recombination rate of electron-hole pairs was significantly decreased. A highest TC removal efficiency of ~99% was observed for 4% CeO 2 /TiO 2 composite for a period of 80 min of visible-light irradiation. Moreover, 88.2% TC mineralization efficiency was achieved for a period of 240 min of visible light irradiation. The enhanced catalytic-activity could be attributed to the synergy of high degree of adsorption followed by an enhanced photocatalysis at the heterointerface formed by the adjacent contact between TiO 2 and CeO 2 . The synergistic effects of low-particle size, high surface-area, enhanced visible-light absorption, reduced band-gap, and increased life-time of the photogenerated charge-carriers through the formation of heterointerface contributed to its high photocatalytic activity. The hydroxyl and superoxide-anion radicals played a superior role in the photocatalytic process. Moreover, the composites retained its efficiency for seven-cycles of reaction without any significant-loss in its activity and structural and textural stability.
危险品化学品经营许可证（带存储）