Polymer precursor synthesis of novel ZrC–SiC ultrahigh-temperature ceramics and modulation of their molecular structure

In this study, ZrC–SiC composite ceramics were prepared with varying Zr/Si molar ratios using sol–gel method. Composites were characterized by Fourier-transform infrared spectroscopy (FT–IR), X-ray diffraction (XRD), thermogravimetric analysis (TGA), transmission electron microscopy (TEM), scanning electron microscopy (SEM), Raman spectroscopy , and energy-dispersive X-ray spectroscopy (EDS). FT–IR analysis confirmed macromolecular network structure of composites, in which the precursor is composed of polyvinyl butyral (PVB) as main chain, silane molecules are interlinked via –OH moieties in PVB side chains, and Zr atoms are crosslinked with Si in corresponding proportion. Ceramic precursor begins to decompose at a temperature exceeding 1300 °C and is completely transformed into ZrC–SiC composite ceramics with corresponding Zr/Si molar ratio at 1600 °C. Raman spectroscopy and TEM results reveal that after annealing at 1600 °C, ZrC powder uniformly covers surface of SiC ceramics, and high-crystallinity graphite carbon covers ZrC powder.