Synthesis of spindle-shaped nanoporous C–LiFePO4 composite and its application as a cathodes material in lithium ion batteries

In this work, LiFePO 4 /C composites were prepared in hydrothermal system by using iron gluconate as iron source, and two feeding sequences during the preparation were comparatively studied. The morphology, crystal structure and charge–discharge performance of the prepared samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), and galvanostatic charge–discharge testing. The results showed that the feeding sequences and iron gluconate seriously affected the microstructures and electrochemical properties of the resulting LiFePO 4 cathodes in lithium ion batteries. The spindle-shaped LiFePO 4 with hierarchical microporous structure self-assembled by nanoparticles has been successfully synthesized by synthesis route B. In addition, the cell performance of the synthesized LiFePO 4 by synthesis route B was better than that of LiFePO 4 by synthesis route A. Specially at high rates, the superior rate performance of the spindle-shaped LiFePO 4 /C microstructure (LFP/C-B) was revealed. And special reversible capacities of ∼118 and ∼95   mAh   g −1 were obtained at rates of 2   C and 5   C, comparing to ∼96 and ∼68   mAh   g −1 for LFP/C-A.