Ultrahigh detectivity ultraviolet photodetector based on orthorhombic phase CsPbI3 microwire using temperature self-regulating solar reactor

In this study, a temperature self-regulating solar reactor based on VO 2 thermochromic coating is demonstrated. The temperature of solar reactor can be stabilized at 68.8 °C, which is corresponded to the critical point of metal-to-insulator transition of VO 2 . By employing the solar reactor, the orthorhombic phase CsPbI 3 microwires have been synthesized through solution phase reaction route. Strong emission peaks at 490 nm and 470 nm have been observed in CsPbI 3 microwires under ultraviolet and soft X-ray excitation, respectively. The high performance photodetector based on CsPbI 3 microwire show a detectivity of 1.09 × 10 14 Jones, responsivity of 4.72 A/W, rapid rise and decay time of 0.96 and 0.93 s at 325 nm. Our results demonstrate that the temperature self-regulating solar reactor can be applied for energy-saving solution phase reactor for synthesizing high quality inorganic materials.