High-temperature performance of all-solid-state battery assembled with 95(0.7Li2S-0.3P2S5)-5Li3PO4 glass electrolyte

Sulfide glasses with a high lithium-ion conductivity are promising solid electrolyte for all-solid-state lithium-ion batteries. In this study, 95(0.7Li 2 S–0.3P 2 S 5 )–5Li 3 PO 4 glass electrolyte is prepared by mixing 70Li 2 S-30P 2 S 5 (mol%) glass and Li 3 PO 4 crystal using mechanical milling technique. The effects on the structures and electrochemical properties of the obtained ternary sulfide glass were examined. The ternary sulfide glass shows a good electrochemical stability, which may exhibit a wide electrochemical window up to 10   V (vs. Li/Li + ). Furthermore, the 95(0.7Li 2 S-0.3P 2 S 5 )-5Li 3 PO 4 glass electrolyte displays an electrical conductivity of 2.513   ×   10 −   3   S   cm −   1 at 100   °C. The all-solid-state lithium-ion cell assembled with 95(0.7Li 2 S-0.3P 2 S 5 )-5Li 3 PO 4 glass electrolyte shows a favourable cyclability, which can reveal a discharge capacity of 144   mAh   g −   1 at 0.05   °C and a discharge capacity of 63.9   mAh   g −   1 at 0.1C after the 50th cycle at 100   °C, respectively.