Effect of TiB2 Pretreatment on Pt/TiB2 Catalyst Performance

Carbon support corrosion of traditional Pt/C catalyst is one of the major contributors causing poor durability of proton exchange membrane fuel cells (PEMFC). Titanium diboride (TiB 2 ) has high electrical conductivity and considerable chemical stability, which making it as a good candidate for catalyst support in PEMFC. In this work, TiB 2 was pretreated by different acid and alkali. The as-obtained samples were characterized by Ex-situ microscopy (ESM) and X-ray diffraction (XRD). The pore size distribution (PSD) was analyzed by using DFT method. The PSD shows distinct volume in mesopore regions (less than 50   nm). The TiB2 pretreated by H 2 O 2 shows the biggest BET surface area of 57   m 2   g −1 and its PSD focus on mesoporous (1.5-8   nm) region, which resulted to high dispersion and better loading of Pt particles. The Hydrogen oxidization reaction (HOR) and oxygen reduction reaction (ORR) activity was characterized by Rotating Disk Electrode (RDE). The Pt/TiB 2 prepared by H 2 O 2 -pretreated TiB 2 using the colloidal method showed better half-cell electrochemical performance. Facile synthetic for the development of Pt/TiB 2 catalysts was developed.