Chemoselective hydrogenation of cinnamaldehyde over MOFs-derived M2Si@C (M = Fe, Co, Ni) silicides catalysts

Chemoselective hydrogenation of C C and C O bonds in the cinnamaldehyde (CMA), was successfully performed with highly dispersed transition metal silicides-embedded in the porous carbon matrix (M 2 Si@C (M = Fe, Co, Ni)) nanocatalysts with a particle size of 8–12 nm, which were synthesized by a facile approach via microwave-assisted chemical vapor deposition (MWCVD) using organosilane and metal-organic-framework (MOFs-74)-templated porous carbon matrix-encapsulated transition metal (M@C) precursors. Compared with M@C, the activity of M 2 Si@C (M = Fe, Co, Ni) nanocatalysts obviously increases, which can be attributed that the overlayered carbon on metals has been destroyed during MWCVD processing, leading to the exposure of more active sites of catalysts. Due to the inherent electronic properties of metallic active sites in the metal silicides, the catalytic activity of Ni 2 Si@C was much higher than that of Co 2 Si@C and Fe 2 Si@C in the chemoselective hydrogenation of CMA. At total conversion of CMA, the Co 2 Si@C nanocatalyst was chemoselective for the hydrogenation of polar C O bonds (selectivity to cinnamyl alcohol of ∼60%), whereas Ni 2 Si@C nanocatalyst was highly chemoselective for the hydrogenation of non-polar C C bonds (selectivity to hydrocinnamaldehyde of ∼90%). The doping of silicon atoms with more electropositive into metals lattices in the M-Si intermetallic compounds (IMCs) influenced the adsorption of substrate molecule on the catalyst surface, slightly leading to the different reaction routes. In addition, the Co 2 Si@C and Ni 2 Si@C respectively maintain the robust stability in the hydrogenation of CMA. This result provided guidance on the design of catalyst via tuning the polarization properties of the inter-atoms in the IMCs according to the target product.