Plasma Oxidation of H2S over Non-stoichiometric LaxMnO3 Perovskite Catalysts in a Dielectric Barrier Discharge Reactor

In this work, plasma-catalytic removal of H2S over LaxMnO3(x= 0.90, 0.95, 1, 1.05 and 1.10) has been studied in a coaxial dielectric barrier discharge (DBD) reactor. The non-stoichiometric effect of the LaxMnO3catalysts on the removal of H2S and sulfur balance in the plasma-catalytic process has been investigated as a function of specific energy density (SED). The integration of the plasma with the LaxMnO3catalysts significantly enhanced the reaction performance compared to the process using plasma alone. The highest H2S removal of 96.4% and sulfur balance of 90.5% were achieved over the La0.90MnO3catalyst, while the major products included SO2and SO3. The missing sulfur could be ascribed to the sulfur deposited on the catalyst surfaces. The non-stoichiometric LaxMnO3catalyst exhibited larger specific surface areas and smaller crystallite sizes compared to the LaMnO3catalyst. The non-stoichiometric effect changed their redox properties as the decreased La/Mn ratio favored the transformation of Mn3+to Mn4+, which contributed to the generation of oxygen vacancies on the catalyst surfaces. The XPS and H2-TPR results confirmed that the Mn-rich catalysts showed the higher relative concentration of surface adsorbed oxygen (Oads) and lower reduction temperature compared to LaMnO3catalyst. The reaction performance of the plasma-catalytic oxidation of H2S is closely related to the relative concentration of Oadsformed on the catalyst surfaces and the reducibility of the catalysts.