Fabricating novel PVDF-g-IBMA copolymer hydrophilic ultrafiltration membrane for treating papermaking wastewater with good antifouling property

Ultrafiltration membranes are widely used for the treatment of papermaking wastewater. The antifouling performance of polyvinylidene fluoride (PVDF) ultrafiltration membranes can be improved by changing the hydrophilicity. Here, a novel amphiphilic copolymer material, PVDF grafted with N-isobutoxy methacrylamide (PVDF-g-IBMA), was prepared using ultraviolet-induced Cu(II)-mediated reversible deactivation radical polymerization. The amphipathic copolymer was used to prepare ultrafiltration membrane via NIPS. The prepared PVDF-g-IBMA ultrafiltration membrane was estimated using 1 H NMR, FT-IR, and DSC. The contact angle, casting viscosity, and the permeation performance of the PVDF-g-IBMA ultrafiltration membrane were also determined. The pure water flux, bovine serum albumin removal rate, and pure water flux recovery rate of the PVDF-g-IBMA ultrafiltration membrane were 432.8 L·m −2 ·h −1 , 88.4%, and 90.8%, respectively. Furthermore, for the treatment of actual papermaking wastewater, the chemical oxygen demand and turbidity removal rates of the membrane were 61.5% and 92.8%, respectively. The PVDF-g-IBMA amphiphilic copolymer ultrafiltration membrane exhibited good hydrophilicity and antifouling properties, indicating its potential for treating papermaking wastewater. A novel amphiphilic copolymer PVDF-g-IBMA prepared by UV-induced RDRP. Good hydrophilic and anti-fouling properties of PVDF-g-IBMA copolymer UF membrane. The MWCO, BSA rejection rate and pure water recovery ratio were 43.7 kDa, 88.4% and 90.8%, respectively. For treating actual papermaking wastewater, the COD removal rate reached 61.5%.