Regulating Li⁺ Solvation Structure of Locally Concentrated Ionic Liquid Electrolytes with Different Fluorinated Diluents for Lithium Metal Batteries

Both TFETFE and 2FB enhance Li⁺-anion interaction, increasing AGGs contents. • 2FB promotes Li⁺-anion interaction more effectively than TFETFE, forming more AGGs. • Inorganic-rich SEI and CEI are generated by deep decomposition of anions in PPB. • Li|PPB|LFP full battery displays a capacity retention of 83.6% after 150 cycles. Due to the low viscosity and weak polarity, fluorinated ethers and fluorinated aromatic compounds are widely used as fluorinated diluents in locally concentrated ionic liquid electrolytes (LCILEs) to improve the electrochemical performance of ionic liquid electrolytes (ILEs). However, the extent to which these two types of diluents regulate Li + solvation structure remains unclear. In this work, two LCILEs were designed using 1,1,2,2-tetrafluoroethyl 2,2,2-trifluoroethyl ether (TFETFE) and 1,2-difluorobenzene (2FB) as diluents, denoted as PPT and PPB, respectively. Raman spectroscopy reveals that both TFETFE and 2FB can strengthen the interaction between Li⁺ and anion, thereby promoting the formation of aggregate ion pairs (AGGs). Compared with TFETFE, 2FB exhibits a more pronounced ability to enhance Li⁺-anion interaction, increasing the proportion of AGGs in PPB electrolyte to 42%, which is significantly higher than that in PPT electrolyte (30%). The enriched AGGs facilitates the preferential reduction and deep decomposition of FSI⁻ at the electrode/electrolyte interphase, leading to the formation of inorganic-rich (LiF, Li 3 N, Li 2 S and Li 2 O) solid electrolyte interphase (SEI) and cathode electrolyte interphase (CEI) with the compact and uniform morphologies. Benefiting from the favorable interfacial chemistry, Li||Cu half battery based on PPB electrolyte delivers a high Li plating/stripping Coulombic efficiency (CE) of 98.7% at 1 mA·cm -2 , exceeding that of PPT (98.0%). In addition, the Li||Li symmetric battery exhibits stable cycling for 160 hours at 2 mA·cm -2 . The Li|PPB|LFP full battery further retains 83.6% of its initial capacity after 150 cycles with an average CE of 99.8%, demonstrating superior electrochemical performance. This work provides practical guidance for the rational selection and structural design of diluents for high performance lithium metal battery electrolytes. Download: Download high-res image (231KB) Download: Download full-size image