JOURNAL OF MATERIALS SCIENCE
·
2022
·Vol. 57
·期 36
·17481-17490
·
IF 4.682
Mo Peicheng,Chen Jiarong,Chen Chao,Hu Qiaofan,Pan Xiaoyi,Xiao Leyin,Lin Feng
Polycrystalline cubic boron nitride (PCBN) was synthesized at high temperature and ultra-high pressure, using cBN, TiN, AlN and Ti as starting materials. The effects of CBN content (48–63 wt%) and sintering temperature (1300–1600 °C) on the composition, microstructure and mechanical properties of PCBN materials were studied. X-ray diffraction and scanning electron microscope were used to analyze the phase composition, microstructure and surface crack morphology of PCBN. At the same time, the compactness, microhardness, fracture toughness and flexural strength of PCBN were tested. Research shows that the phase components of PCBN samples are mainly composed of BN, TiB 2 , TiN and AlN. Almost all Ti reacts with cBN during the sintering process to form TiN and TiB 2 phases. When the sintering temperature is 1500 °C, the reaction has been fully completed. When the cBN content increases from 48 to 63 wt%, the relative density, flexural strength and hardness of PCBN increase with the increase in cBN content. When sintered at 1500 °C and the cBN content is 63 wt%, the relative density, flexural strength, fracture toughness and microhardness of the composite are 99%, 820.8 MPa, 6.6 MPa.m 1/2 and 3362 Hv, respectively.
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
·
2022
·Vol. 32
·期 9
·4270-4282
·
IF 2.036
Zhang Kaige,Ding Jianxiang,Ding Kuankuan,Xia Xinxin,Chen Liming,Ma Chengjian,Zhang Peigen,Sun ZhengMing
This work investigates the influence of sintering temperature on phase constitution, microstructure, and properties of Ti 2 AlC-reinforcing Ag-based composite. Part of active Al atomic layer in Ti 2 AlC migrates outward under the induction of relatively low sintering temperature (≤ 800 °C) and then generates the Ti-Al compounds and TiC. By means of elemental analysis, obvious Ag-Al inter-diffusion is detected at Ag-Ti 2 AlC interface at 900 °C and then Al-deficient layer forms around slightly dissociated Ti 2 AlC particles. At elevated temperature (950 °C), more significant interface diffusion and dissociation accelerate the decomposition and oxidation of Ti 2 AlC and subsequently generate mixture of titanium and aluminum oxides (Ti x O y , Al x O y ). The oxides’ agglomeration and residual Ti 2 AlC lead to form network-like and ravine-like structure. The moderate Ag-Al inter-diffusion slightly increases the resistivity (94.59 × 10 −3 μΩ·m), but contributes to improving the interface bonding and mechanical properties (106 HV hardness, 298.6 MPa tensile strength) of Ag/Ti 2 AlC at 900 °C. However, the severe Ti 2 AlC decomposition and oxides agglomeration account for the significant deduction in electrical conductivity (132.79 × 10 −3 μΩ·m) and mechanical properties (87 HV, 222.3 MPa) at 950 °C. A mechanism is proposed to further understand the phase transition, microstructure evolution, and interface reaction of the Ag/Ti2AlC with the elevated sintering temperature.
✓ 已验证
产品关联
DOI
高影响因子
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS
·
2022
·
IF 4.804
Chen Chao,Mo Peicheng,Chen Jiarong,Hu Xixi,Hu Qiaofan,Lin Feng,Wu Yi
Using TiN-Ti-AlN as the binder, polycrystalline cubic boron nitride (PCBN) composites containing Y 2 O 3 and not containing Y 2 O 3 were prepared under high temperature and ultra-high pressure conditions, respectively. X-ray diffraction (XRD) and scanning electron microscope (SEM) were used to analyze the phase composition, microstructure and surface crack morphology of the composite material. At the same time, the compactness, microhardness and bending strength of the composite material were tested. The research results show that the phase composition of PCBN sample is mainly composed of BN, TiB 2 , TiN, AlN and Y 2 O 3 at an ultra-high pressure of 5.5 GPa and a temperature of 1500 °C. With the increase of Y 2 O 3 content, the relative density of PCBN first increases and then decreases, and the changes in mechanical properties also tend to be similar. As the content of Y 2 O 3 increases, it can be seen that the peak intensity of the main peak of TiB 2 also increases, indicating that the addition of Y 2 O 3 promotes the reaction between cBN and Ti. When the Y 2 O 3 content is 3.6%, PCBN has the best comprehensive mechanical properties, with a microhardness of 34.56 GPa and a bending strength of 890 MPa.
✓ 已验证
产品关联
DOI
高影响因子
ACS Omega
·
2022
·
IF 4.132
Xing-hao Han,Chuan-qi Li,Ping Tang,Chen-xiao Feng,Xin-zheng Yue,Wen-lei Zhang
Titanium dioxide (TiO2) micro-nanostructures are widely utilized in photochemical applications due to their unique band gaps and are of huge demand in scientific research and industrial manufacture. Herein, this work reports a controllable, facile, economical, and green solid-phase synthesis strategy to prepare TiO2 with governable morphologies containing 1D nanorods, 3D microbulks, and irregular thick plates. Specifically, Ti powders are transformed into TiO2 micro-nanostructures through dispersing them into a solid NaOH/KOH mixture with a low eutectic point, followed by grinding, heating, ion exchange, and calcination. As no solvents are utilized in the alkali treatment process, the usage of solvents is decreased and high vapor pressure is avoided. Moreover, the band gaps of TiO2 micro-nanostructures can be regulated from 3.02 to 3.34 eV through altering the synthetic parameters. Notably, the as-prepared TiO2 micro-nanostructures exhibit high photocatalytic activities in the degradation of rhodamine B and methylene blue under simulated solar light illumination. It is believed that the solid-phase synthesis strategy will be of huge demand for the synthesis of TiO2 micro-nanostructures.
✓ 已验证
产品关联
DOI
PubMed
高影响因子
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
·
2022
·
IF 6.044
Zeyun Cai,Tao Xiang,Weizong Bao,Jiayin Chen,Tian Gao,Guoqiang Xie
Pure titanium is an ideal material for tissue replacements and implant materials for its superior biocompatibility and corrosion resistance , but its limited strength remains a major obstacle to its wide applications. A promising strategy for enhancing the strength is to alloy the pure titanium with oxygen. Herein, we reported an oxygen solid solution strengthening for pure titanium by achieving a titanium-oxygen (Ti–O) alloy using ball milling (BM) and spark plasma sintering (SPS). The effect of oxygen contents, ranging from 0.33 to 2.08 wt%, on the mechanical properties of pure titanium was systematically investigated. Experimental results indicate that the Ti–O alloy with the oxygen content of 1.95 wt% reached an ultrahigh yield strength of 2026 MPa and showed a large ductility of 11.2% in compression. According to the quantified analysis of strengthening mechanisms, solid solute oxygen atoms are responsible for the balance of superior yield strength and ductility of the Ti–O alloys.
✓ 已验证
产品关联
DOI
高影响因子
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
·
2022
·
IF 6.044
Hao Wang,Fei Chen,Jiahao Zhao,Yaojun Lin,Qiang Shen
This paper presents a method of dealloying combined molten salt electrolysis (MSE) to prepare porous Ti alloy. The oxidation produced in dealloying process can be reduced efficiently by MSE. Meanwhile, the grain grew and the second phase of acicular nanocrystals was precipitated to enhance the mechanical properties during MSE process.
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF COLLOID AND INTERFACE SCIENCE
·
2021
·
IF 8.128
Xiaoming Wang,Qianqian Peng,Xilin Zhang,Xucheng Lv,Xin Wang,Yongzhu Fu
Refractory high-entropy alloy nanocomposites (HEA-NPs) are important class of materials with unique structure and potential applications. Although several synthetic methods have been reported, developing novel routes to prepare nanoscale HEA-based catalysts facilely is still urgently desired. This work takes advantage of confinement assisted arc and plasma shock (APS) to prepare a series of HEA-NPs by regulating the type and proportion of metal precursors. The phase constitutes and morphology of the HEA-NPs are fully characterized. The prepared refractory HEA-NPs possesses five highly dispersed metal components, including titanium (Ti), niobium (Nb), tantalum (Ta), chromium (Cr), molybdenum (Mo) and simultaneously exhibits an uniform hexagonal morphology of nanocrystals . By taking advantage of its unique corrosion resistance , TiNbTaCrMo HEA-NPs can function as a promising candidate for electrocatalytic hydrogen evolution reaction (HER) in natural seawater . And its catalytic performance after alloying is significantly enhanced compared with the elemental metal. Theoretically, the promoted HER activity can be attributed to the strong adsorption for the various metal components in HEA-NPs caused by the upshifting d -band center close to the Fermi level . Furthermore, this confinement strategy can be further extended to synthesize other HEA-NPs. Our strategy provides a novel method to synthesize various HEA-NPs for further catalytic application.
✓ 已验证
产品关联
DOI
PubMed
高影响因子
Small
·
2021
·Vol. 17
·期 40
·2103239
·
IF 13.281
Yanhong Duo,Guanghong Luo,Zihuang Li,Zide Chen,Xianming Li,Zhenyou Jiang,Binlu Yu,Hao Huang,Zhengbo Sun,Xue-feng Yu
Nanomaterial-based photothermal and photocatalytic therapies are effective against various types of cancers. However, combining two or more materials is considered necessary to achieve the synergistic anticancer effects of photothermal and photocatalytic therapy, which made the preparation process complicated. Herein, the authors describe simple 2D titanium diselenide (TiSe 2 ) nanosheets (NSs) that can couple photothermal therapy with photocatalytic therapy. The TiSe 2 NSs are prepared using a liquid exfoliation method. They show a layered structure and possess high photothermal conversion efficiency (65.58%) and good biocompatibility. Notably, upon near-infrared irradiation, these NSs exhibit good photocatalytic properties with enhanced reactive oxygen species generation and H 2 O 2 decomposition in vitro. They can also achieve high temperatures, with heat improving their catalytic ability to further amplify oxidative stress and glutathione depletion in cancer cells. Furthermore, molecular mechanism studies reveal that the synergistic effects of photothermal and enhanced photocatalytic therapy can simultaneously lead to apoptosis and necrosis in cancer cells via the HSP90/JAK3/NF-κB/IKB-α/Caspase-3 pathway. Systemic exploration reveals that the TiSe 2 NSs has an appreciable degradation rate and accumulates passively in tumor tissue, where they facilitate photothermal and photocatalytic effects without obvious toxicity. Their study thus indicates the high potential of biodegradable TiSe 2 NSs in synergistic phototherapy for cancer treatment.
✓ 已验证
产品关联
DOI
PubMed
高影响因子
POWDER METALLURGY
·
2022
·
IF 2.228
Ying Zhang,Meng Xiao,Yi-min Zhou,Yi-fu Shen
The eutectic FeNiCoCrTi0.6Nb0.4 high-entropy alloy coating (HEAC) is annealed in Argon at 450°C, 850°C and 1050°C to investigate the thermal stability. The results show that annealed coatings are all composed of BCC solid solution and Laves phase with no production of new phases. The fine eutectic cells can be maintained at a higher temperature in that continuous intracellular coarsening does not occur until annealing at 1050°C. With the increase of annealing temperature, the microhardness and wear resistance of FeNiCoCrTi0.6Nb0.4 coating increase first and then decrease slightly. Especially, the microhardness of FeNiCoCrTi0.6Nb0.4 annealed at 1050°C is only 6.03% lower than that of unannealed one, and the wear rate is only 10.70% higher than that of unannealed one, which strongly indicates that eutectic FeNiCoCrTi0.6Nb0.4 HEAC has excellent thermal stability and can be well applied in high-temperature environments.
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
·
2021
·
IF 8.067
Wei Luo,Yi Liu,Chuangye Wang,Dan Zhao,Xiaoyan Yuan,Jianfeng Zhu,Lei Wang,Shouwu Guo
The morphology of MAX phase powders significantly influences their microwave absorption properties. However, the traditional synthesis via solid-state reactions produces irregular powders, and the preparation of MAX phase powders with specific morphology remains a challenge. Herein, (V 0.8 Ti 0.1 Cr 0.1 ) 2 AlC MAX phase microrods were fabricated for the first time in NaCl/KCl molten salts using vanadium, titanium, chromium, aluminum , and short carbon fibers as precursors. It was found that despite acting as a carbon source, carbon fibers also acted as sacrificial templates. By adjusting the molar ratio of metal powders and short carbon fibers, a series of carbon fiber@(V 0.8 Ti 0.1 Cr 0.1 ) 2 AlC microrods with core-sheath structure were also obtained. Carbon fiber@(V 0.8 Ti 0.1 Cr 0.1 ) 2 AlC microrods with a molar ratio of 8:2 showed the optimum microwave absorption performance. The reflection loss (RL) value reached up to –63.26 dB at 2.40 mm, and the effective absorption bandwidth (EAB) was about 5.28 GHz with a thickness of 2.02 mm. Based on the electromagnetic parameter analysis and theoretical simulation, the enhanced microwave absorption performance was attributed to the synergistic effect of different factors like dielectric loss, magnetic loss, multiple reflection, and scattering. This work offers a facile route to modulate the morphology of MAX phase powders and may accelerate its application as microwave absorbers.
✓ 已验证
产品关联
DOI
高影响因子
COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS
·
2021
·
IF 4.539
Yefeng Feng,Peiyao Chen,Bingshuang Mao,Maolin Bo,Qihuang Deng
Ultrahigh dielectric constant is obtained in polymer/MXene composites due to percolation . However, huge dielectric loss is triggered owing to high leakage current . In this work, hybrid filler consisting of Ti 2 C MXene and ZrO 2 was prepared for coordinating high dielectric constant and low dielectric loss in composites. Instead of Ti 2 C percolation, Ti 2 C/ZrO 2 interface effect mildly increased dielectric constant. Ultrahigh insulation and large aspect ratio of ZrO 2 fibers significantly reduced dielectric loss. Binary polymer/Ti 2 C and ternary polymer/Ti 2 C-ZrO 2 composites were fabricated, and better overall electric traits in ternary system were found. Ti 2 C/ZrO 2 interface effect was studied using density functional theory (DFT) calculations. Ternary composite with 12 wt% filler exhibited high dielectric constant of ~40, low dielectric loss of ~0.09 at 100 Hz and high breakdown strength of ~155 MV m −1 . This work might impulse fabrication of MXene-based hybrid fillers for dielectrics.
✓ 已验证
产品关联
DOI
高影响因子
ACS Applied Energy Materials
·
2021
·
IF 6.024
Yiming Zhang,Yubing Si,Wei Guo,Xiang Li,Shuai Tang,Zhaoxin Zhang,Xin Wang,Yongzhu Fu
The practical application of lithium–sulfur batteries (LSBs) is partially impeded by large volume variation, severe shuttle effect, and inferior electrical conductivity of sulfur. On this account, a template-free arc-discharge method for the synthesis of TiSx (1.5 < x < 2)@HCN (hollow carbon nanocage) as an efficient sulfur host is developed for LSBs. TiSx@HCN can accommodate the volume changes of active materials and inhibit the shuttle effect of lithium polysulfides (LiPSs). Theoretical calculation shows that the defective titanium sulfide accelerates the conversion of long-chain LiPSs to intermediate species and promotes the redox reactions. As a consequence, the resulting hybrid cathode composited with sulfur exhibits excellent electrochemical performances. A reversible capacity of 1118.6 mA h g–1 is obtained under 0.1 C with a slow capacity decay of 0.108% per cycle for 200 cycles. The synthetic strategy provides a facile platform for the synthesis of nanocomposite materials.
✓ 已验证
产品关联
DOI
高影响因子