RSC Advances
·
2016
·Vol. 6
·期 86
·83288-83295
·
IF 3.289
Chongmin Liu,Shuai Liu,Pingxiao Wu,Yaping Dai,Lytuong Tran,Nengwu Zhu,Chuling Guo,Ihsanullah Sohoo
Modified calcium saturated montmorillonite (Mt) was prepared at different 3-aminopropyltriethoxysilane (APTES) loadings through grafting. The as-products were characterized by XRD, FTIR and elemental analysis. Surface analysis such as acidity was examined at different H+ concentrations, showing that the release of OH− from the modified samples increased in the following order: APTES4.0CEC–Mt > APTES3.0CEC–Mt > APTES2.0CEC–Mt > APTES1.0CEC–Mt. Batch experiments were conducted and different conditions (pH, temperature and co-existing ions) were used to evaluate the adsorption capacity of the modified samples. The study developed a new way to confirm the mechanism, which indicated that ligand adsorption was the dominant sorption mechanism for Sr(II) uptake onto APTES–Mts. In general, APTES grafted montmorillonite possessed a higher efficiency of Sr(II) uptake and showed great potential for Sr(II)-rich wastewater treatment.
研究领域:
环境科学
·
材料科学
·
化学工程
·
环境污染治理
·
吸附科学
✓ 已验证
DOI
高影响因子
JOURNAL OF MEMBRANE SCIENCE
·
2015
·
IF 5.056
He Chen,Liang Kong,Yong Wang
Activation by nitric acid oxidation has been combined with atomic layer deposition (ALD) to modify microporous polypropylene (PP) membranes. Nitric acid oxidation with prewetting of t -butanol generates active groups on the inert surface of PP membranes. Metal oxides including Al 2 O 3 and TiO 2 are subsequently ALD-deposited on the activated membrane. Nitric acid oxidation is a mild approach to activate PP membranes. A short immersion in nitric acid for 10 min is able to generate oxygen/nitrogen-containing active species on the membrane surface , which leads to an evident increase (38%) in the membrane permeability. The mechanical stability and the integrity of the porous structure are well preserved after activation. Surface elemental analyses and microscopy observations confirm the successful deposition of metal oxides thin layers onto the activated membranes. In the deposition of either Al 2 O 3 or TiO 2 , the hydrophilicity of the deposited membranes is continuously improved with increasing ALD cycles, resulting in further increase in water flux. After 100 ALD cycles, the flux is doubled compared to that of the bare membrane. Al 2 O 3 is more efficient in enhancing the hydrophilicity and permeation than TiO 2 under identical deposition conditions because of the faster growth of Al 2 O 3 on the activated PP surface.
研究领域:
材料科学
·
膜技术
·
表面化学
·
高分子化学
·
化学工程
✓ 已验证
DOI
高影响因子
JOURNAL OF COLLOID AND INTERFACE SCIENCE
·
2019
·
IF 6.361
Hashim Sliman,Xue Dong,Tao Zhao
In recent years, increasing environmental awareness and human skin protection from harmful radiation of the sun has attracted attention amongst numerous researchers. Here, a simple strategy was developed to enhance the hydrophilicity and ultraviolet (UV) protection of polyethylene terephthalate (PET) knitted fabric surface via grafting green cowpea protein (CP) with gum arabic modified epoxy (GAE) as a cross-linking agent. Chemical grafting between pretreated PET and GAE as well as between GAE and CP improved the hydrophilicity and UV protection of PET knitted Fabric. The enhanced surface wettability was confirmed by the decreased water contact angle from 135° to zero °. Moreover, the UV protection factor rating of modified PET knitted fabric was higher, indicating that the modifier layer caused scattering and absorbance of UV light. This approach has shown promising results for improving hydrophilicity and UV protection with sustained mechanical durability of 7 washing cycles.
研究领域:
材料科学
·
纺织化学
·
表面工程
·
生物高分子
·
功能纺织品
✓ 已验证
DOI
高影响因子
Asia-Pacific Journal of Chemical Engineering
·
2021
·Vol. 16
·期 6
·e2702
·
IF 1.447
Shiyuan Xiong,Xiaole Huang,Wennian Xu,Xiaoping Guo,Shuan Liu
In previous work, the corrosion performance and anti-corrosion mechanism of galvanized steel wire embedded in vegetation-growing concrete under marine environment was highlighted. In this work, a graphene-modified epoxy coating was developed and applied to the protection of galvanized steel in vegetation-growing concrete under a marine environment. The effect of dispersed graphene on the anticorrosion performance of the epoxy coatings was evaluated. The composite coatings displayed outstanding barrier properties against H 2 O molecules compared to the pure epoxy coating. Salt spray test results revealed superior corrosion resistance offered by the prepared graphene-modified epoxy coating on galvanized steel.
研究领域:
材料科学
·
腐蚀与防护
·
土木工程材料
·
复合材料
·
环境耐久性
✓ 已验证
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2019
·Vol. 45
·期 8
·10633-10639
·
IF 3.45
Guorong Hu,Zhichen Xue,Zhongyuan Luo,Zhongdong Peng,Yanbing Cao,Weigang Wang,Yuexi Zeng,Yong Huang,Yong Tao,Tianfan Li,Zhiyong Zhang,Ke Du
The Li-rich cathode material for long cycle performance and long-term storage performance is a challenge for next-generation lithium-ion batteries due to the rapid capacity degradation over cycling and the formation of residual lithium on the surface during long-term storage. Herein, an elevated performance of Li 1.2 Mn 0.54 Ni 0.13 Co 0.13 O 2 materials via CeO 2 inlay is reported, which was prepared from Li 1.2 Mn 0.54 Ni 0.13 Co 0.13 O 2 by sol-gel inlay with CeO 2 . It was proved by scanning electron microscopy, high-resolution transmission electron microscopy, X-ray diffraction and X-ray photoelectron spectroscopy that cerium oxide cladding not only covered the surface of the material but also diffused into the interior of the material change crystal structure. Cerium oxide on the cladding not only reduces the material's contact with water and carbon dioxide in the air, but also prevents the material from being corroded by electrolyte during electrochemical test. The position of the transition metal atom is replaced Ce atoms, which increases the unit cell volume and the stability of the Li-rich material during the cycling. The results show that the storage property and the electrochemical cycling property of the material have been improved obviously. The CeO 2 inlaid lithium rich material discharged 204.6 mAh/g for the first time at the current of 1C, and 164.4 mAh/g after 150 charge and discharge cycles with corresponding capacity retention rate of 80.35%, compared with the retention rate of 57.26% for pristine Li-rich material capacity. After being stored in humid air for 40 days, the CeO 2 inlaid lithium-rich material showed better electrochemical performance than the pristine one. It is powerfully demonstrated that the CeO 2 inlay strategy here holds huge promise for surface modification of electrode materials for lithium-ion batteries.
研究领域:
材料科学
·
电化学
·
锂离子电池
·
能源存储
·
无机非金属材料
✓ 已验证
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2016
·Vol. 42
·期 6
·7767-7773
·
IF 2.758
Shuangbing Li,Jixiao Wang,Song Zhao,Wei Cai,Zhi Wang,Shichang Wang
The unmodified and 3-(trimethoxysilyl) propyl methacrylate (TPM) modified silica nanoparticles were synthesized via the modified Stöber method. The structure and chemical composition of silica nanoparticles were determined by scanning electron microscope (SEM), X-ray diffraction (XRD) characterization, Fourier Transform Infrared Spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). The results demonstrate that silica nanoparticles with the diameter of 90 nm and amorphous state are successfully modified by TPM. The rheological test results demonstrated that surface modification of nanoparticles and medium exerted great influence on the rheological properties of silica particle suspension. Under high shear rate of about 250 s −1 , the viscosity of suspension comprising unmodified silica nanoparticles and deionized water , TPM-modified silica nanoparticles and deionized water, TPM-modified silica nanoparticles and polyethylene glycol , is about 0.4 Pa.s, 0.1 Pa.s and 30 Pa.s, respectively. The results are significant for preparing homogenous and stable silica nanoparticle suspension, and meaningful for ceramic processing .
研究领域:
材料科学
·
纳米技术
·
陶瓷加工
·
胶体化学
·
高分子材料
✓ 已验证
DOI
高影响因子
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING
·
2016
·Vol. 122
·期 5
·515
·
IF 1.444
Huang Liang,Zhu Pengli,Li Gang,Sun Rong
The partial reduced graphene oxide (P-rGO) sheets-wrapped nickel foams (NF@P-rGO) were prepared by hydrothermal method, and then their epoxy composites were fabricated via a simple drop-wetting process. The P-rGO sheets on the metal networks could effectively improve the compatibility between nickel foam and epoxy resin, thus greatly accelerate the wetting of epoxy resin on the foams and avoid cracks in the network–polymer interface. Owing to the existence of high-efficiency conductive metal networks, the NF@P-rGO/epoxy composite has a high thermal conductivity of 0.584 W m −1 K −1 , which is 2.6 times higher than that of neat epoxy resin. Additionally, owing to the improved wetting ability, NF@P-rGO-10 wt% boron nitride (BN) microsheets/epoxy composites could be fabricated and have a further higher thermal conductivity of 0.71 W m −1 K −1 . We believe the use of P-rGO as a novel surface modifier and the following liquid polymer drop-wetting could be an effective method to obtain novel and outstanding metal foam/polymer composites.
研究领域:
材料科学
·
高分子复合材料
·
热管理材料
·
表面与界面工程
✓ 已验证
DOI
高影响因子
Journal of the Taiwan Institute of Chemical Engineers
·
2019
·
IF 3.834
Xiao Wang,George Q. Chen,Wei Zhang,Huining Deng
The development of reliable anion exchange membranes (AEMs) with superior antifouling properties is critical in practical applications of electrodialysis processes. For the first time, the AEMs were modified by poly (sodium 4-styrene sulfonate) (PSS) with titanium dioxide (TiO 2 ) nanoparticles using only one electrodeposition step to stabilize the nanoparticles on the membrane surface while improving their antifouling ability. Owing to the bonding between the sulfonic groups of PSS and TiO 2 , the TiO 2 nanoparticles were well dispersed in the modified layer. The deposition of PSS endowed the AEMs with a negatively charged surface, while the addition of TiO 2 nanoparticles further increased the charge density. The membrane resistance increased only marginally after 100-min of fouling experiments using sodium dodecyl benzene sulfonate (SDBS), due to the presence of TiO 2 on the modified AEMs. Ultraviolet (UV) irradiation was proven to be an effective approach in inducing good fouling reversibility of the TiO 2 -PSS modified AEMs through photocatalytic decomposition and hydrophilicity improvement.
研究领域:
膜科学
·
环境工程
·
材料化学
·
电化学
·
水处理技术
✓ 已验证
DOI
高影响因子
JOURNAL OF APPLIED POLYMER SCIENCE
·
2016
·Vol. 133
·期 35
·
IF 1.866
Yuanzhu Long,Fuhua Sun,Chao Liu,Dong Huang,Xingyi Xie
To explore a new blowing agent for polyurethanes (PUs), palmitic acid was grafted onto a branched polyethyleneimine (bPEI; weight-average molecular weight = 25,000 Da) via N,N ′-carbonyldiimidazole condensation to form a hydrophobically modified bPEI [palmitic acid grafted branched polyethyleneimine (C 16 –bPEI)] with a grafting rate of 12%. A CO 2 adduct of C 16 –bPEI, which trapped 16.8% CO 2 in it, was synthesized from C 16 –bPEI. The long alkyl chain grafting improved the dispersibility of the CO 2 adduct in the PU raw materials and favored a homogeneous release of CO 2 to blow PUs during the exothermic foaming process. The preliminary results show that the foams possessed a density of 72.0 kg/m 3 and a compressive strength of 246 kPa; this matched the required values of foams for the thermal insulation of underground steel pipes. This new blowing agent emitted nothing but CO 2 to the atmosphere, so it will not promote ozone depletion and will avoid global warming problems that are associated with traditional blowing agents such as chlorofluorocarbons and hydrochloroflourocarbons. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133 , 43874.
研究领域:
高分子化学
·
材料科学
·
绿色化学
·
能源与环境材料
·
工业催化
✓ 已验证
DOI
高影响因子
Journal of Materials Research and Technology-JMR&T
·
2023
·
IF 6.4
Jinhui Wang,Ruisong Wang,Xiaoxiao Ji,Chunde Jin,Yutao Yan
Phenol formaldehyde (PF) resin adhesives are widely used in the production of bamboo-based composites owing to their excellent bonding strength and durability. However, the inherent brittleness of cured PF resin may result in notable stress concentration at the interface between PF resin and bamboo bonding, leading to the generation of cracks. In this study, a hyperbranched compound polyethyleneimine (PEI) with high reaction activity was incorporated into a PF resin adhesive to toughen the adhesive and the bonding interface. And the effects of PEI incorporation on the properties of the adhesive and the bonding performance between PF resin and bamboo were comprehensively investigated. The results showed that introduction of flexible PEI chains could effectively facilitated stress transfer, avoiding stress concentration, thus enabling efficient energy release and play a toughening effect. In addition, PEI could react with PF resin and bamboo components during hot pressing, forming a three-dimensional network structure and enhancing the bonding interface, which was proved by FT-IR and XPS analysis. When 1 wt% PEI was incorporated, the bending strength and Charpy impact toughness of the modified PF resin was significantly increased by 38.88% and 76.02%, respectively, compared with the pure PF resin. While the dry and wet shear strength of the bamboo composite bonded by the PEI modified PF resin were also obviously increased. This study is expected to address the problem of cracking in the bonding interface of bamboo composite, and endow the composites with high strength and durability, which can prolong its service life and contribute to the healthy and sustainable development of the bamboo industry.
研究领域:
材料科学
·
木材科学与技术
·
高分子化学
·
复合材料工程
·
胶接与界面科学
✓ 已验证
DOI
高影响因子
JOURNAL OF FOOD BIOCHEMISTRY
·
2021
·Vol. 45
·期 4
·e13647
·
IF 2.72
Yiqin Zhang,Honglei Mu,Haiyan Gao,Hangjun Chen,Weijie Wu,Yanchao Han,Xiangjun Fang,Chuan Tong
Mechanical damage and microbial infestation were critical issues during strawberry transportation. This study prepared a modified polyvinyl formal (PVFM) vibration-damping material and investigated its application in strawberry transportation. This modified PVFM was primarily composed of polyvinyl alcohol, starch, formaldehyde, and allyl isothiocyanate. Our results showed that the modified PVFM had good vibration-damping and antifungal properties with 0.137 g/m 3 of density, a water absorption ratio value of 6.24, 278 Pa of tensile strength, 3.86 Pa of elastic modulus, a buffer coefficient of 0.318, and antifungal rates of 68.8% and 80.6% against Bacillus anthracis and Botrytis cinerea , respectively. Moreover, this modified PVFM could enhance the storage life of strawberry by improving PAL activity from 376 to 3,125 U/g, inhibiting POD activity with a maximum value of 3.1 U/g, and decreasing CAT activity from 324 to 35 U/g. The modified PVFM presented a good vibration-damping capacity and the potential to extend strawberry shelf life. Practical applications Berry fruits were vulnerable to mechanical damage caused by vibration during transportation, resulting in quality deterioration, rot, and aging. In this study, modified polyvinyl formal (PVFM) was prepared and was of low density and displayed good mechanical, vibration-damping, and antifungal properties. The modified PVFM could improve the storage life of strawberry. Thus, the modified PVFM could have potential application in berry fruits transportation.
研究领域:
食品科学
·
农产品贮藏与加工
·
高分子材料学
·
园艺产品采后生理
·
包装工程
✓ 已验证
DOI
高影响因子
JOURNAL OF MEMBRANE SCIENCE
·
2018
·
IF 6.578
Shaosuo Bing,Jiaqian Wang,Hao Xu,Yanyan Zhao,Yong Zhou,Lin Zhang,Congjie Gao,Li’an Hou
Polyamide (PA) thin-film composite (TFC) reverse osmosis membrane is widely used for desalination , but the selectivity-permeability trade-off and oxidation are two major restrictions on the membrane application. By modifying PA TFC membrane with potassium persulfate (K 2 S 2 O 8 ), we overcame the trade-off relation (the water flux and salt rejection increased by 43.2% and 0.2%, respectively) and improved the chlorine resistance. The modification was demonstrated to be a combination of the interfacial crosslinking between PA layer and polysulfone support with the surficial oxidation of PA layer. The dense crosslinked interface enabled the membrane with higher solute rejection, better chlorine tolerance and long-term stability. Meanwhile, the thinner PA layer contributed to the increase of membrane permeability. Furthermore, the modification method has the application potential in high-performance membrane fabrication in terms of simplicity and high efficiency.
研究领域:
材料科学
·
膜分离技术
·
高分子化学
·
环境工程
·
水处理
✓ 已验证
DOI
高影响因子