Zhaowang Dong,Yang Xia,Xueyi Guo,Jinlong Zhao,Linfeng Jiang,Qinghua Tian,Yong Liu
Upgraded titania slag (UGS) is a titanium-rich material with over 90 wt% titanium dioxide and some minor elements such as Fe, Al, Cr, and Si, which is mainly used for preparing TiO 2 and TiCl 4 . In this study, UGS was directly reduced with magnesium powder in a hydrogen atmosphere. Titanium alloy hydride powder with the oxygen content of 0.032 wt% was obtained. The minor elements of Fe, Si, Al, and Cr from the UGS were kept in the final powder with the main phase of TiH 1.924 (δ), and minor intermetallic phases of HFe 2 Ti, Ti 5 Si 3 H 0.9 and Cr 1.8 TiH 5.3 . EDS elemental mapping results indicated that HFe 2 Ti and Ti 5 Si 3 H 0.9 intermetallics formed bright phase islands in the matrix. The reduction mechanism and the reaction sequence were discussed based on the thermodynamic modelling with the assistance of HSC chemistry software. The possibility of hydrogen reduction of titanium oxides was discussed as well.
Yongqi Da,Xiaodong Ma,Tingshu He,Renhe Yang,Yang Li,Qianqian Yang,Jing Du
The titanium-bearing pickling (TP) sludge from titanium processing industry is the hazardous solid waste that remains to be utilized harmlessly and resourcefully. It consists of 34 % calcium, 18 % fluorine, 15 % titanium and high leaching toxic of heavy metals, but the most of TP sludge was still landfilled with huge environmental hazards, and the utilization studies are rare. Hence, the study proposed to upcycle this sludge by the light calcination modification, the effects of calcined lightly TP sludge (LTP sludge) on cement properties and leaching safety were investigated by XRD, SEM, MIP, BCR, etc. The results revealed that light calcination (600 °C/700 °C/800 °C for 2h) assisted the formation of anatase and fluorite, and induced transformation from anatase to rutile, the calcined LTP sludge presented larger particle size, smaller specific surface area and the different microstructure. The addition of TP sludge into cement even induced the water requirement reach 33.2 % couple with the prolonged setting time and weak strength, the calcined LTP sludge reversed the above inhibition effects, its addition could accelerate hydration process, dense the hydrated matrix with improved pore distribution and lower porosity, also reduce water requirement, shorten setting time and promoted the strength. The 3d and 28d compressive strength of cement prepared with 15 % calcined LTP sludge under 600 °C reached 27.7 Mpa and 52.9Mpa. Gradual formation of fluorite, rutile and anhydrite in calcined LTP sludge under 800 °C might lead to the deceleration in cement hydration couple with the reduced strength. The amounts of mobile and hazardous metal speciation in the TP sludge are higher than 40 %, but after light calcination modification, F1, F2 and F3 fractions have transformed into F4 (higher than 92 %) in hydrated cement prepared with calcined LTP sludge under 600 °C, the harmful ions hardly escaped from the hydrated matrix and even in the various pH leaching environments.
危险品化学品经营许可证（带存储）