International Journal of Applied Ceramic Technology
·
2024
·
IF 1.8
Yiming Yu,Yaowu Wei,Kui Liu,Bo Chen,Junfeng Chen
This paper aims to improve the density and thermal shock resistance of Y 2 O 3 ceramics for the preparation of ultra-pure high-temperature alloy crucible materials. The doping effect of MgF 2 content on the densification behavior, physical properties, and thermal shock resistance of Y 2 O 3 ceramics was systematically investigated in this paper. The results suggested that the presence of MgF 2 greatly promoted the growth of Y 2 O 3 grains and the transformation of the pore structure by liquid-phase sintering. And the mechanical properties of the MgF 2 -doped Y 2 O 3 ceramics were significantly improved. Besides, the marked improvement in the thermal shock resistance of MgF 2 -doped Y 2 O 3 ceramics was attributed to the synergistic action resulting from the growth of grain size and the enhancement of the crack deflection effect. In particular, the relative density of Y 2 O 3 ceramics doped with 1.5 wt% MgF 2 reached 96.4% and the residual flexural strength ratio after thermal shock achieved 45.0%, showing an excellent application prospect.
研究领域:
材料科学
·
陶瓷工程
✓ 已验证
产品关联
DOI
高影响因子
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
·
2021
·
IF 5.234
X.F. Xie,K. Jing,Z.M. Xie,R. Liu,J.F. Yang,Q.F. Fang,C.S. Liu,Xuebang Wu
Bulk pure tungsten (W), W-0.5 wt%TiC (WTC05) and W-1 wt%Y 2 O 3 (WY10) materials were prepared by a developed two-step hot-pressing (HP) sintering method. Metallographic observation, SEM and TEM characterization were conducted to obtain the information of material microstructures . The results indicate that a small amount of TiC or Y 2 O 3 addition could effectively improve the sinterability and reduce the grain size of the HP sintered WTC05 and WY10 alloys. The relative density of WTC05 and WY10 reaches as high as 99%, and the average grain size of WTC05 and WY10 are 2.61 μm and 3.57 μm, respectively, which are several times smaller than that of pure W. Among the three W materials, pure W has the poor tensile performance with insufficient strength and ductility, WTC05 has the highest tensile strength with the ultimate tensile strength of 1082 MPa at 300 °C, and WY10 has the best ductility and moderate strength. The relationship between the microstructures and the tensile properties has been investigated, and suggestions on microstructure parameters have been proposed for preparing high performance W-based materials.
研究领域:
材料科学
·
金属学
✓ 已验证
DOI
高影响因子
SENSORS AND ACTUATORS B-CHEMICAL
·
2021
·
IF 7.46
Chu Cheng,Jie Zou,Yucun Zhou,Zi Wang,Han Jin,Guangzhong Xie,Jiawen Jian
A mixed potential type alcohols gas sensor based on an yttrium stabilized zirconia (YSZ) electrolyte and an La 0.8 Sr 0.2 MnO 3 (LSM) sensing electrode was fabricated. The influences of YSZ-LSM interface on sensing performance were studied by multiple methods including X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), thermogravimetric analysis and differential scanning calorimetry (TG-DSC) and electrochemical impendence spectroscopy (EIS). The sensor with 1150 °C-sintered interface showed an ultralow detection limit of 50 ppb alcohols (methanol and ethanol) at 500 °C in air. The response voltage was independent of water, CO, CO 2 and NO x . The sensor exhibited a reasonable selectivity towards alcohols under the existence of several kinds of volatile organic compounds. Meanwhile, the sensor showed a good repeatability and a suitable long-term stability. Based on the polarization curves and EIS results, a mixed potential mechanism was proposed. These results demonstrate the promising potential of using the LSM-based sensor for human exhale test.
研究领域:
材料科学
·
电化学
✓ 已验证
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2023
·
IF 5.2
Zhuangzhuang Ma,Lu Chen,Jian Chen,Wang Guo
This paper presents the successful homogeneous processing of Y 2 O 3 green compacts by pressure-assisted alcoholic slip casting (PASC) method for the preparation of high-quality Y 2 O 3 transparent ceramics. The optimal Y 2 O 3 alcoholic slurry with 1.5 wt% polyethyleneimine as the dispersant and the solid load of 30.69 vol% was employed for PASC. Compared to dry-pressing green compact, PASC-prepared green compact exhibits high homogeneity and sinterability with less microstructural defects, such as large pores or particle agglomeration . Based on these advantages, we successfully prepared transparent Y 2 O 3 ceramic by simply vacuum sintering with low porosity, excellent optical homogeneity, and high in-line transmittance of 80.4% at the wavelength of 600 nm.
研究领域:
材料科学
·
陶瓷加工技术
✓ 已验证
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2022
·
IF 5.532
Haoran Li,Yan Liu,JinJing Yang,Ming Yuan,Anle Sun,Tiesong Lin,Xuejian Liu,Zhengren Huang
A new La 2 O 3 -doped Y 2 O 3 crucible materials was fabricated and evaluated by TiAl alloys melting test. Microstructure and properties of the La 2 O 3 -doped Y 2 O 3 ceramics were systemically investigated. In addition, interfacial reaction mechanism of the La 2 O 3 -doped Y 2 O 3 crucible materials and TiAl alloys, together with oxygen content of TiAl alloys were discussed. Solid solution of La 3+ in the crystal lattice of Y 2 O 3 significantly improved sintering properties of the La 2 O 3 -doped Y 2 O 3 crucible materials and decreased the open porosity. Compared with pure Y 2 O 3 , when adding 15 wt% La 2 O 3 , the open porosity and strength retention ration after thermal shock test of the La 2 O 3 -doped Y 2 O 3 crucible materials changed from 10.8% to 3.9% and from 64% to 78%, respectively. The interfacial reaction between La 2 O 3 -doped Y 2 O 3 crucible materials and TiAl alloys belongs to physical dissolution, and no reaction products were found during the melting of TiAl alloys. When using the 15 wt% La 2 O 3 -doped Y 2 O 3 crucible materials to melt TiAl alloys, oxygen content of the TiAl ingot declined to 530 ppm, which was only one fourth of that using pure Y 2 O 3 materials.
研究领域:
材料科学
·
冶金工程
✓ 已验证
产品关联
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2025
·
IF 5.6
Chenguang Li,Junbin Sun,Weihong Lu
The corrosion caused by air sediments comprising CaO-MgO-Al 2 O 3 -SiO 2 (CMAS) poses a notable challenge to thermal/environmental barrier coatings as engine service temperatures continue to rise. In this study, three types of Y 2 O 3 -SiO 2 binary compound ceramic bulks—Y 2 SiO 5 , Y 2 SiO 5 -Y 2 Si 2 O 7 and Y 2 Si 2 O 7 —with molar ratios of Y 2 O 3 :SiO 2 of 1:1, 1:1.5, and 1:2, respectively, were prepared and subjected to CMAS corrosion at 1250 °C and 1350 °C for durations ranging from 1 to 10 h. The corrosion products and cross-sectional morphologies of the samples were characterized using X-ray diffraction and scanning electron microscope. The results demonstrate that the material composition determines its CMAS corrosion behavior. Y 2 SiO 5 , with higher Y 2 O 3 content, consumes more CaO to form Ca 2 Y 8 (SiO 4 ) 6 O 2 , thereby reducing the CaO content and increasing the viscosity of the residual CMAS melt. This process inhibits further CMAS penetration. The findings highlight a novel strategy to improve CMAS corrosion resistance by modifying the CMAS composition and reducing its penetration capability.
研究领域:
材料科学
·
无机非金属材料
·
高温腐蚀与防护
·
陶瓷基复合材料
✓ 已验证
产品关联
DOI
高影响因子
KEY ENGINEERING MATERIALS
·
2016
·
IF 0
Shen Qi,Xiao Jian Mao,Bao Yan Chai,Long Zhang
Transparent aluminum oxynitride (AlON) ceramics have been prepared through a method based on direct reaction sintering of alumina and aluminum nitride powders using MgO and Y2O3 as co-additives. The sintering additives could cause the formation of liquid phase during sintering, which would greatly promote the densification and eliminate pores. The grain size of AlON is about 50-100μm. The influence of different component of Al2O3 and AlN as well as sintering temperature on microstructure and optical properties of AlON have been studied. High transparent AlON ceramics with the in-line transmittance of 80.3% at 2000 nm wavelength have been prepared when the concentration of sintering additives was 0.16wt% Y2O3 and 0.02wt% MgO.
研究领域:
材料科学
·
光学工程
✓ 已验证
DOI
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
·
2024
·
IF 8.1
Yajing Hu,Yong Men,Shuyi Xu,Yuanfen Feng,Jinguo Wang,Kaijie Liu,Yibo Zhang
Constructing the interface of Ni/Y 2 O 3 heterogeneous catalyst is a feasible strategy for efficient catalyst design in CO 2 methanation, which can create the active Y–O–Ni interfacial sites by utilizing the interaction between Ni and Y 2 O 3 . In this work, the strategy of using different nickel precursors (nickel nitrate, nickel acetate, basic nickel carbonate and nickel citrate) was used to prepare various Ni-based catalysts supported on Y 2 O 3 , which were estimated for their catalytic performance on CO 2 methanation. The catalysts were characterized based on BET, XRD, TEM, H 2 -TPR, XPS and CO 2 -TPD, etc. The results indicated a close correlation between the metal dispersion and particle size of Ni/Y 2 O 3 catalysts and the nickel precursor employed. The Y–O–Ni interface structure in Ni/Y 2 O 3 catalysts, associated with basic sites, provides a richer source of basic sites, offering more active sites for CO 2 adsorption and activation. Ni/Y 2 O 3 catalyst prepared with nickel nitrate as the precursor exhibited characteristics such as a highly enhanced nickel dispersion, a smaller nickel particle size, and more abundant metallic Ni 0 sites. Moreover, nickel nitrate-derived Ni/Y 2 O 3 catalyst exhibited optimal catalytic activity, achieving a CO 2 conversion rate of up to 92 % at 300 °C, with 100 % selectivity to CH 4 , and displaying good stability over 30 h. Therefore, the dispersion of Ni and the size of Ni particles could be controlled by adjusting the precursor, which is closely associated with the catalytic activity of Ni/Y 2 O 3 catalyst. This work unveils the interface-property relationship of Ni/Y 2 O 3 catalysts and provides a new insight into strategy of constructing more effective Ni-based catalyst for CO 2 methanation through the controlled nickel precursor.
研究领域:
催化化学
·
材料科学
·
环境科学
✓ 已验证
产品关联
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2015
·
IF 2.605
Meng Zhao,Xiaorui Ren,Jun Yang,Wei Pan
A series of ThO 2 -doped Y 2 O 3 stabilized ZrO 2 monolith compounds were prepared and investigated. The bigger ionic radius of Th 4+ substitutions dilutes the average oxygen coordination to the cations, which is the determinant factor of the phase stability. Therefore, ThO 2 incorporation has a strong impact on the phase composition, and consequently on the thermo-mechanical properties of the specimens. The metastable t′ phase was stabilized in light-doped specimens with a decreasing tetragonality while the thermodynamic equilibrium t phase and the related martensitic t–m phase transformation were absent in ThO 2 -doped specimens. Additionally, lower thermal conductivity was also achieved due to the substitutional phonon scattering effect. Considering the phase stability and thermo-mechanical properties, ThO 2 -doped Y 2 O 3 stabilized ZrO 2 compounds may be promising candidates for thermal barrier coatings although further research may be needed to improve their mechanical properties.
研究领域:
材料科学
·
热物理
✓ 已验证
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2023
·
IF 5.2
Miao Zhou,Yun Liu,Xiaolei Li,Tianyi Sui,Dong Su,Huiming Ji
Silicon nitride (Si 3 N 4 ) ceramics were prepared by gas-pressure sintering using Y 2 O 3 –MgSiN 2 as a sintering additive. The densification behavior, phase transition, and microstructure evolution were investigated in detail, and the relevance between the microstructure and the performance (including thermal conductivity and mechanical properties) was further discussed. A significant change from a bimodal to a homogeneous microstructure and a decreased grain size occurred with increasing Y 2 O 3 –MgSiN 2 content. When the small quantity of preformed β-Si 3 N 4 nuclei grew preferentially and rapidly in a short time, an obvious bimodal microstructure was obtained in the sample with 4 mol% and 6 mol% Y 2 O 3 –MgSiN 2 . When more β-Si 3 N 4 nuclei grew at a relatively rapid rate, the sample with 8 mol% Y 2 O 3 –MgSiN 2 showed a microstructure consisting of numerous abnormally grown β-Si 3 N 4 grains and small grains. When more β-Si 3 N 4 nuclei grew simultaneously and slowly, there was a homogeneous microstructure and smaller grains in the sample containing 10 mol% Y 2 O 3 –MgSiN 2 . Benefitting from the completely dense, significant bimodal microstructure, low grain boundary phase, and excellent Si 3 N 4 –Si 3 N 4 contiguity, the sample containing 6 mol% Y 2 O 3 –MgSiN 2 exhibited great comprehensive performance, with a maximum thermal conductivity and fracture toughness of 84.1 W/(m⋅K) and 8.97 MPa m 1/2 , as well as a flexural strength of 880.2 MPa.
研究领域:
材料科学
·
陶瓷工程
✓ 已验证
产品关联
DOI
高影响因子
PHYSICA B-CONDENSED MATTER
·
2021
·
IF 2.436
Yihang Dong,Zhaoyang Liu,Lipeng Pang,Ye Han,Shuyu Yao,Xiangnan Wang
{(Y 2 O 3 ) 0·08 (ZrO 2 ) 0.92 } 1- x (CeO 2 ) x (0 ≤ x ≤ 0.6) is synthesized by co-precipitation method. Thermal analysis, phase structure, lattice constant , micro-morphology, elements distribution, density, open porosity and electrical conductivity are measured by TG, DSC , XRD , GSAS, SEM , EDS, Archimedes method and EIS respectively, and the influence of CeO 2 content on the above properties are investigated. TG-DSC results show that the weight loss of the sample is mainly due to the decomposition of the initial powder, forming a solid solution above ~600 °C. XRD results show that {(Y 2 O 3 ) 0·08 (ZrO 2 ) 0.92 } 1- x (CeO 2 ) x (0 ≤ x ≤ 0.6) is a cubic solid solution, and the lattice parameters and volume increase with the increase of CeO 2 content. SEM results show that YZC is a dense sintered body. Density and open porosity of YZC sample are ~4.5 g cm −3 and ~0.12, respectively. The electrical conductivity results show that the conductivity of {(Y 2 O 3 ) 0·08 (ZrO 2 ) 0.92 } 1- x (CeO 2 ) x (0 ≤ x ≤ 0.2) is equivalent, and then the conductivity decreases due to defect association with the increase of CeO 2 content.
研究领域:
材料科学
·
陶瓷材料
✓ 已验证
产品关联
DOI
高影响因子
VACUUM
·
2022
·
IF 4.11
Xinjiang Zhang,Ziqing Chen,Zhaohui Liu,Meng He,Zirun Yang,Jiahui Wang
The in-situ hybrid particle-reinforcements are a novel strengthening mode for the advanced metal matrix composites . In this study, Zr matrix composites incorporating the fixed amount of ZrC particles with the different amounts of Y 2 O 3 particles were prepared by the in-situ reaction among Zr, graphite, Y, and ZrO 2 during the arc-melting. Results revealed that the graphite/Zr reaction produced the uniform in-situ ZrC particles in the Zr matrix, and the Y/ZrO 2 reaction formed the Y 2 O 3 particles. In-situ Y 2 O 3 addition refined the Zr matrix and led to the polygonal morphology of the ZrC particle. The coarser Y 2 O 3 grew in bulk, and some fine Y 2 O 3 dendrites were formed along Zr boundaries. The influence of different contents of Y 2 O 3 reinforcements on the hardness and compressive properties were analyzed. Compared with the single ZrC reinforcements, the hybrid Y 2 O 3 introduction resulted in a higher hardness and enhanced compressive strength . This hybrid structures were believed to be favorable to mechanical responses in the composites, and the relevant mechanisms for the hardening and strengthening effect of such hybrid forms were discussed.
研究领域:
材料科学
·
力学
✓ 已验证
产品关联
DOI
高影响因子