Full-spectrum phosphor-converted white-light-emitting diodes (pc-WLED) are emerging as a mainstream technology in semiconductor lighting. Nevertheless, high-performance blue phosphor which can be excited efficiently by a 400 nm NUV diode chip is still lacking. Herein, we present a blue-emitting Na 3 KMg 7 (PO 4 ) 6 :Eu 2+ phosphor synthesized by the solid-reaction method. Particularly, we find that the using of Li 2 CO 3 as flux can significantly improve the crystal quality and thus the emission efficiency of the phosphor. Meanwhile, the excitation peak of the phosphor shifts from 365 to 400 nm, which is pivotal for efficient NUV (400 nm) diode chip excitation. The practical Eu 2+ concentration is also enhanced by using Li 2 CO 3 as flux, and the absorption efficiency is greatly increased. This phosphor exhibits superior PL thermal stability, namely retains 94% integrated photoluminescence intensity at 150 °C of that at 25 °C. As a result, the optimized phosphor shows an emission band peaked at 437 nm with a bandwidth of 40 nm and a high external photoluminescence quantum yield of 51.7%. Finally, a pc-WLED was fabricated by using NKMPO:Eu 2+ blue, Sr 2 SiO 4 :Eu 2+ green, CaAlSiN 3 :Eu 2+ red phosphors, and a 400 nm NUV diode chip. It shows a high color rendering index of R a = 96.4 and a correlated color temperature of 4358 K. These results prove that NKMPO:Eu 2+ is a promising blue phosphor for full-spectrum WLED based on NUV diode chips.
We report luminous polylactic acid (PLA) composite prepared via a solvent casting method using different amounts of phosphor strontium aluminate (SrAl2O4: Eu2+ and Dy3+) (SAO). The reason for doing this is that the changes of fluorescence and mechanical properties in the composites with different SAO contents can be directly evaluated. The SAO particles should have a variety of excellent characteristics in the PLA matrix, among which dispersibility and compatibility are particularly important; so, they can be modified by 3-aminopropyltriethoxysilane (APS) to achieve the target characteristics. The results showed that the fluorescence and mechanical properties were affected by SAO addition. The mechanical properties significantly improved with 5 wt% SAO; further, addition had no impact. And the emission band of fluorescence and phosphorescence is just at the peak of 524 nm. The composites with 15 wt% SAO have the best fluorescence properties. The fluorescence decreased with further doping. Fluorescence decay curves with various amounts of SAO particles show a similar tendency as pure SAO particles; the speed of decrease in afterglow intensity was higher for the first 30 min. In addition, the detailed morphological scanning and study by scanning electron microscope (SEM) showed that the particles had good adhesion to the matrix. In conclusion, the concentration of SAO into the PLA matrix impacts the fluorescence and mechanical properties of a SAO/PLA composite material.
危险品化学品经营许可证（带存储）