SPECTROCHIMICA ACTA PART A-MOLECULAR AND BIOMOLECULAR SPECTROSCOPY
·
2023
·
IF 4.4
Jie Fu,Yanling Chen,Jianhua Lin,Renguang Ye,Lei Lei,Yang Shen,Degang Deng,Shiqing Xu
Bi 3+ , Eu 3+ co-doped Ba 2 Y 2 Si 4 O 13 phosphors with multi-color luminescence properties were prepared by high temperature solid state method. The structure, luminescent properties and temperature characteristics were studied by X-ray diffraction, scanning electron microscope, fluorescence spectrum and temperature-dependence of emission spectrum. Ba 2 Y 2 Si 4 O 13 : Bi 3+ , Eu 3+ phosphors can emit color from cyan to red when the excitation wavelength was changed from 340 nm to 390 nm, which is attributed to that there are two Bi 3+ ion emission centers, and their emission intensity will change with the change of excitation wavelength. Moreover, the emission of the phosphor has good temperature sensing characteristics, based on the fluorescence intensity ratio of the two blue emission bands of Bi 3+ and the red emission peak of Eu 3+ , a multimode thermometer with high temperature sensitivity was constructed. At the same time, based on the dynamic luminescence characteristics of the phosphor, the dynamic anti-counterfeiting experiments are designed. Therefore, the results show that the material has a bright prospect in the field of temperature sensing and anti-counterfeiting.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
PubMed
高影响因子
CERAMICS INTERNATIONAL
·
2024
·
IF 5.1
Wei Meng,Xiaoyan Fu,Chunqing Fu,Wenzhi Sun,Changsheng Wang,Hongwu Zhang
Here, we have developed a novel ultra long ultraviolet-A afterglow material CaMgGeO 4 : Bi 3+ , which shows more than 24 h UVA afterglow emission peaked at 346 nm. The crystal structure shows that the prepared sample is a pure phase with an orthogonal system of Pmnb space group. The composition of valence band and conduction band was analyzed by the density of states , which reveals that the bandgap of the CaMgGeO 4 matrix is 3.69 eV. The photoluminescence spectrum of the sample consists of a broadband in the 320–400 nm UVA region, which belongs to the 3 P 1 → 1 S 0 electron transition of Bi 3+ . More importantly, under the excitation of ultraviolet lamp for 3 min, CaMgGeO 4 : Bi 3+ exhibited an UVA ultra long persistent luminescence (LPL) with a duration of more than 24 h, which afterglow emission intensity still reaches 1500 cps and is about 6 times of the background intensity. In addition, the UVA emission of CaMgGeO 4 : Bi 3+ after 13 h day can be repeatedly by short periods of low-energy light sources stimulation. The thermoluminescence analysis indicates that the presence of shallow and deep traps is responsible for excellent UVA-LPL and photo-stimulate luminescence (PSL). The excellent LPL and PSL properties can prompt CaMgGeO4: Bi 3+ phosphor to be widely used in the field of photodynamic therapy.
研究领域:
材料科学
·
光学
✓ 已验证
DOI
高影响因子
JOURNAL OF ALLOYS AND COMPOUNDS
·
2024
·
IF 5.8
Yu-Xi Bi,Dan Zhao,Shao-Jie Dai,Rui-Juan Zhang,Qing-Xia Yao
Ion doping is one of the most effective strategies to induce interesting luminescence properties of materials. In this work, the Bi 3+ and Eu 3+ are introduced into a ‘114’ host material YBaZn 3 GaO 7 (YBZG) to generate photoluminescence (PL), long-persistent luminescence (LPL) and colour change properties. The co-doped YBZG:0.003Bi 3+ / y Eu 3+ can generate multi-color emissions from green, through yellow to orange with the increasing of Eu 3+ concentration. There are F-like color centers around conduction band (CB) of YBZG host with shallow or deep energy levels. The electrons trapped by deep levels response to the PC properties, whereas these for shallow levels response to the LPL properties. The PC process from white to apricot is reversible. By alternating thermal treatment and irradiation, YBZG:0.003Bi 3+ was proved to have a good fatigue resistance of 3.1 %. For YBZG:0.003Bi 3+ /0.05Eu 3+ , it shows bright orange LPL emission when the irradiation is removed after 24 min. The achievement of this paper provides a design idea that if the host structure of a phosphor is of flexible and easy to occur defect, not only PL property, but also PC and LPL properties are probably able to realize.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
·
2015
·Vol. 27
·期 4
·3514-3519
·
IF 1.569
Cao Renping,Fu Ting,Cao Yunling,Jiang Shenhua,Gou Qingdong,Chen Zhiquan,Liu Pan
Novel CaSb 2 O 6 :Eu 3+ , Bi 3+ phosphor is synthesized by solid-state reaction method in air. Their crystal structures are investigated. Luminescence properties of CaSb 2 O 6 :Eu 3+ , CaSb 2 O 6 :Bi 3+ , and CaSb 2 O 6 :Eu 3+ , Bi 3+ phosphors are compared, analyzed and explained, respectively. Tunable emission of CaSb 2 O 6 :Eu 3+ , Bi 3+ phosphor with excitation 298 nm can be observed by changing Eu 3+ or Bi 3+ concentration. Energy transfer (ET) and charge compensation in CaSb 2 O 6 :Eu 3+ , Bi 3+ phosphor are observed and analyzed via its luminescence properties. Lifetimes of CaSb 2 O 6 :5 %Eu 3+ , yBi 3+ phosphor (0.5 ≤ y ≤ 5 mol%) are investigated, which further confirm that ET process can be formed between Eu 3+ ion and Bi 3+ ion. The luminous mechanism is explained via the energy level diagrams of Bi 3+ and Eu 3+ ions. The emission properties indicate that CaSb 2 O 6 :Eu 3+ , Bi 3+ phosphor has a potential application for white LEDs based on near UV (~394 nm) LED chip.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF MOLECULAR STRUCTURE
·
2023
·
IF 3.8
Renping Cao,Jingyi Lin,Bang Lan,Fangrui Cheng,Ting Chen,Lan Li,Ru Liu,Jing Wang
Na 3 Sc 2 (PO 4 ) 3 :R (R = Bi 3+ , Sm 3+ , and Sm 3+ /Bi 3+ ) are successfully synthesized in air atmosphere. The high-temperature solid-state reaction method is used in this work. The X-ray diffractometer patterns confirm that all samples have the single pure phase Na 3 Sc 2 (PO 4 ) 3 . Na 3 Sc 2 (PO 4 ) 3 :Bi 3+ displays blue emission because of the Bi 3+ - Sc 3+ metal-to-metal charge-transfer and the 3 P 1 → 1 S 0 transition of Bi 3+ . Na 3 Sc 2 (PO 4 ) 3 :Sm 3+ shows red-orange emission with four emission bands derived from the 4 G 5/2 → 6 H 5/2 (550 - 582 nm), 6 H 7/2 (582–625 nm), 6 H 9/2 (625–675 nm), and 6 H 11/2 (675–750 nm) transitions of Sm 3+ . The optimal Sm 3+ concentration in Na 3 Sc 2 (PO 4 ) 3 :Sm 3+ is ∼8mol%. An adjustable color emission from blue to red-orange of Na 3 Sc 2 (PO 4 ) 3 :Sm 3+ , Bi 3+ with excitation at 345 nm can be observed when the ratio between Sm 3+ and Bi 3+ ions is changed. Na 3 Sc 2 (PO 4 ) 3 :Sm 3+ , Bi 3+ emits red–orange light under excitation 406 nm. The optimal Bi 3+ concentration in Na 3 Sc 2 (PO 4 ) 3 :8mol%Sm 3+ , Bi 3+ is ∼ 6mol%. The energy transfer from Bi 3+ to Sm 3+ in Na 3 Sc 2 (PO 4 ) 3 :Sm 3+ , Bi 3+ is verified by the spectral properties of samples. We discuss the influences of Bi 3+ or Sm 3+ concentration on luminescence properties of samples and analyze their luminous mechanism by energy level diagram. The experimental results of paper are useful for the research of new Bi 3+ and Sm 3+ doped phosphors.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
·
2016
·Vol. 27
·期 6
·6188-6192
·
IF 1.798
Wu Yeqiu,Jin Guangya,Liu Zhijian,He Tao
Y 2 O 3 :Eu 3+ and Y 2 O 3 :Eu 3+ /Bi 3+ particles with spherical morphology are synthesized by microwave-assistant hydrothermal process. The results show that cubic phase Y 2 O 3 :Eu 3+ and Y 2 O 3 :Eu 3+ /Bi 3+ particles with uniform size and spherical shape are obtained. The doping Eu 3+ and Bi 3+ ion have no influence on the phase and morphology of samples. In the hydrothermal process, the fast and homogeneous microwave heating benefits the formation of samples with uniform size and spherical shape. Both Y 2 O 3 :Eu 3+ and Y 2 O 3 :Eu 3+ /Bi 3+ show dominant red emission originating from the 5 D 0 → 7 F 2 transition of Eu 3+ . The codoping Bi 3+ can enhance the intensity of Eu 3+ emission.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
MOLECULES
·
2025
·Vol. 30
·期 9
·2028
·
IF 4.6
Jialu Qu,Xingyu Duan,Ke Xue,Shengli An
Solid-state electrolytes (SSEs) have emerged as the most promising alternative to liquid electrolytes in batteries due to their enhanced stability and safety. Among these, the garnet-type Li7La3Zr2O12(LLZO) solid electrolyte has attracted significant research interest due to its wide electrochemical stability window and good air stability. However, the ionic conductivity of LLZO is lower due to its high sintering temperature and unstable phase structure. In this study, Li6.4+xFe0.2La3Zr2−xBixO12(x = 0, 0.05, 0.1, 0.15) solid electrolytes were synthesized using a conventional solid-state reaction method by co-doping LLZO with Fe3+and Bi3+ions. Compared with pure LLZO, doping with Fe3+effectively stabilizes the cubic phase, thereby enhancing the ionic conductivity. Moreover, Bi3+doping significantly lowers the sintering temperature of the electrolyte, which in turn reduces energy consumption during the processing. The co-doping of Fe3+and Bi3+not only improves the density of the LLZO electrolyte, achieving a relative density of up to 95%, but also increases the ionic conductivity, with a maximum value of 7.57 × 10−4S·cm−1observed at the optimal composition (Li6.4+xFe0.2La3Zr2-xBixO12, x = 0.1).
研究领域:
材料科学
·
电化学
✓ 已验证
产品关联
DOI
PubMed
高影响因子
JOURNAL OF RARE EARTHS
·
2023
·
IF 4.9
Danyu Zhang,Yuxuan Luo,Junyu Chen,Lianjie Li,Hai Guo
Dual-excitation and dual-emission Y 4 GeO 8 :Bi 3+ ,Sm 3+ phosphors were manufactured by traditional solid-phase sintering technique. The X-ray diffraction, morphology, photoluminescence, energy transfer process and temperature sensing properties of Y 4 GeO 8 :Bi 3+ ,Sm 3+ samples were comprehensively evaluated. The Y 4 GeO 8 :Bi 3+ ,Sm 3+ phosphors exhibit characteristic emissions of Bi 3+ ( 3 P 1 → 1 S 0 ) and Sm 3+ ( 4 G 5/2 → 6 H) under both 290 and 347 nm excitations. In fluorescence intensity ratio and Commission International de L'Eclairage coordinates modes, Y 4 GeO 8 :Bi 3+ ,Sm 3+ samples present excellent temperature measurement performance. The maximum relative sensitivity ( S r-max ) values of the former are 1.55 %/K (460 K, 290 nm excitation) and 0.82 %/K (506 K, 347 nm excitation). The S r-max ( x ) values of the latter are 0.21 %/K (437 K, 290 nm excitation) and 0.15 %/K (513 K, 347 nm excitation). These results illustrate that Y 4 GeO 8 :Bi 3+ ,Sm 3+ phosphors can be used as a candidate material for a dual-mode optical thermometer under dual-excitation.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
OPTICAL MATERIALS
·
2024
·
IF 3.8
Yanting Liu,Qiumei Li,Lili Meng,Qi Pang,Yanzhu Wang,Hua Yao,Qian Chen
The emergence of near-infrared (NIR) luminescence from lanthanide (Ln 3+ ) ions doped lead-free Cs 2 AgInCl 6 double perovskites (DPs) has garnered significant attention due to its extensive range of potential applications. Unfortunately, they still suffer from weak NIR emission due to the inherent wide band gap of DPs resulting in inefficient energy transfer from the host to Ln 3+ . Herein, Bi 3+ can act as the sensitizer to activate Ho 3+ emission and reduce the excitation energy in Cs 2 AgInCl 6 : Ho. Under 400 nm excitation, Bi 3+ co-doped Cs 2 AgInCl 6 : Ho shows 39 times and 21 times higher emission intensity than Cs 2 AgInCl 6 : Ho in Visible and NIR. As a result, a photoluminescence quantum yield of 18.63 % ranging from 800 to 1600 nm can be obtained. Finally, by coupling a Bi-doped sample with a commercial near-ultraviolet LED chip (395 nm), a compact Vis-NIR ultrawideband light source was prepared, which has promising applications in multifunctional illumination and night vision.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
OPTICAL MATERIALS
·
2023
·
IF 3.9
Mengjia Zhang,Changchun Ding,Bin Duan,Yuxiang Wu,Yongqiang Li,Jin Wei,Fengyi Wang,Junshan Hu
The upconversion luminescence (UCL) of inorganic materials doped with activators and sensitizers has great application, but its luminescence intensity always impose restrictions on its development. Herein, an obvious enhancement in luminescence intensity of the WO 3 : Yb 3+ , Ho 3+ phosphor was realized through non-equivalence substitution of Bi 3+ ions. The single pure phase of the synthesized WO 3 : Yb 3+ , Ho 3+ , and Bi 3+ phosphors has been confirmed by the XRD pattern. The morphology of phosphors and valence state of elements have been performed by SEM and XPS techniques. The sample on excitation with 980 nm performs forceful green emission and weak red emission at 543 nm and 662 nm, separately. The concentrations for doped Yb 3+ and Ho 3+ to obtain the optimal UCL in WO 3 are 8% and 1%, respectively. The optimized doping concentration for Bi 3+ ions is 3%. Compared to samples without Bi 3+ ions, the Yb 3+ /Ho 3+ /Bi 3+ doped WO 3 obtains 1.59 and 2.33 times increase in emission intensity of green and red, respectively. We also explored the UCL mechanism and enhancement mechanism on the basis of the power dependency, the UCL and the downshift luminescence. These results based on Yb 3+ /Ho 3+ UCL phosphors research is of great significance.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子
OPTICAL MATERIALS
·
2022
·
IF 3.754
Fengxia Zou,Ming Li,Zengyan Du,Yi Song,Liang Li,Guanghai Li
In modern agriculture, light plays an important role in plant growth. Far red light controls the whole growth process of plants from germination to vegetative growth to flowering. Here, we report the preparation and photoluminescence (PL) performance of Cr,Bi co-doped SrGdAlO 4 phosphors by solution combustion method. The SrGdAlO 4 :Cr 3+ ,Bi 3+ phosphors exhibit far red broadband PL of 660–780 nm excited at 458 nm, and the maximum emission peak position is at 713 nm. It was found Cr 3+ and Bi 3+ replaced the positions of Al 3+ and Gd 3+ in the host material, respectively. The PL performance of SrGdAlO 4 :Cr 3+ ,Bi 3+ phosphors mainly depends on the 2 E 2 → 4 A 2 transition of Cr 3+ , and the addition of Bi 3+ can effectively enhance the PL intensity of the phosphors. Notably, the SrGdAlO 4 :Cr 3+ ,Bi 3+ phosphors also exhibit obvious far red PL when coated onto glass substrate or mixed with plastics without affecting their visible light transmission. We believe our work will excite interests in further exploring the practical application of SrGdAlO 4 :Cr 3+ ,Bi 3+ phosphors as plant growth regulator in greenhouse.
研究领域:
农业科学
·
材料科学
·
植物生物学
✓ 已验证
DOI
高影响因子
CRYSTAL RESEARCH AND TECHNOLOGY
·
2022
·Vol. 57
·期 4
·2100162
·
IF 1.599
Yanli Ding,Zhaohan Li
The low luminous efficiency of upconversion materials limits their practical applications in various fields. The present study focuses on the efficient upconversion enhancement of β-NaYF 4 :Yb,Er induced by Bi 3+ doping. The XRD and SEM results show that introducing Bi 3+ into the matrix lattice changes the microstructure and particle size of the crystal. The photoluminescence spectra show that at 6% Bi 3+ doping, the red and green emission intensities are enhanced by 12 and 8 times, respectively. The reason could be the lattice distortion caused by Bi 3+ doping, breaking the partial forbidden transition of rare-earth ions. The fluorescence lifetime measurement reveals that the Bi 3+ doping changes the environment around erbium ions, affecting the energy level lifetime of erbium ions, explaining the luminescence dynamics law. The present study provides a facile route to achieve nano/microstructures with intense upconversion luminescence with potential applications in optoelectronic devices.
研究领域:
材料科学
·
光学
✓ 已验证
产品关联
DOI
高影响因子