JOURNAL OF ALLOYS AND COMPOUNDS
·
2019
·
IF 4.175
Yingying Lai,Lizhang Lv,Heqing Fu
In this work, Al 2 O 3 @PPy@rGO composites were successfully synthesized by a “coating-coating” route. The structure of Al 2 O 3 @PPy@rGO composites was characterized by XRD , Raman and SEM. The coaxial wire method was used to measure the electromagnetic properties of Al 2 O 3 @PPy@rGO composites, which was carried on the vector network analyzer (VNA, 3672A/B/C-S) over the 2–18 GHz frequency range. Compared with Al 2 O 3 (about 50 nm), the particle size of Al 2 O 3 @PPy composites (about 70 nm) enhanced, which verified the alumina was coated by PPy . In addition, the Al 2 O 3 @PPy composites are tightly attached by the rGO with a diameter of about 30 nm Al 2 O 3 @PPy@rGO composites have excellent thermal stability, and they remain 53 wt% when the temperature is up to 800 °C. When the thickness of Al 2 O 3 @PPy@rGO composites is 3.0 mm, they reach the maximum reflection loss of −39.7 dB at 13.2 GHz with 15 wt% Al 2 O 3 @PPy@rGO-wax. And the broad effective microwave absorption bandwidth of Al 2 O 3 @PPy@rGO composites is 5.5 GHz in 10.5–16.0 GHz. In addition, the electromagnetic wave absorption mechanism of Al 2 O 3 @PPy@rGO composites was analyzed.
研究领域:
材料科学
·
电磁学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF ALLOYS AND COMPOUNDS
·
2022
·
IF 6.371
Yi-Ran Li,Ying-Ming Li,Bing-Bing Chen,Wen-Juan Hu,De-Yi Wang
Ideal electromagnetic absorbing material should not only be light weight, broadband and high efficient, but also easily prepared and flame-retarding to satisfy the challenges from rapid development of electronic information technology. In present paper, a new type of electromagnetic absorbent (Fe-MOF-rGO) was prepared via a simple one-pot method to grow metal-organic framework (Fe-MOF) on the surface of in-situ reduced graphene oxide (rGO) by solvothermal method. When 25 wt% of Fe-MOF-rGO was incorporated into the paraffin matrix, the minimum reflection loss value (RL) reached to −43.6 dB at the thickness of 2 mm, and the effective absorption bandwidth (EAB) exceeded 5.0 GHz, which satisfied the goals of high efficiency, light weight and broadband. According the medium permittivity loss, magnetization loss and excellent resistance matching results, it was concluded that the conduction loss (excellent conductivity of rGO), magnetic loss (magnetic resonance of Fe nanoparticles) and interface polarization loss (heterostructure of two-dimensional rGO and three-dimensional Fe-MOF) of Fe-MOF-rGO jointly determined the electromagnetic absorbing performance. Moreover, the combustible behavior of Fe-MOF-rGO was also investigated. When 10 wt% of Fe-MOF-rGO was incorporated into the epoxy resin (EP), the heat release capacity (HRC) and peak heat release rate (PHRR) decreased by 42.1% and 42.3% respectively, which showed an excellent flame-retarding property.
研究领域:
材料科学
·
电磁学
·
燃烧学
✓ 已验证
DOI
高影响因子
NANOTECHNOLOGY
·
2016
·Vol. 28
·期 2
·025501
·
IF 3.573
Bingrong Wang,Yang Cao,Yong Chen,Xiaoyong Lai,Juan Peng,Jinchun Tu,Xiaotian Li
NiCo2O4 nanospheres, a type of conjugated reduced graphene oxide (rGO), are compounded by a simple and easy synthesis of Cu2O/GO and fabricated NiCo2O4/rGO nanocomposites based on a Cu2O/GO template. The structure and morphology of the hierarchical NiCo2O4/rGO are characterized by x-ray diffraction, x-ray photoelectron spectroscopy, scanning electron microscopy, and transmission electron microscopy. The electrochemistry properties of NiCo2O4/rGO composites toward glucose are determined based on a glassy carbon electrode, and the results indicate that the hollow nanospheres of NiCo2O4/rGO could achieve high-sensitivity detections of glucose. The NiCo2O4/rGO composite has a detection range of 0.04 mM to 1.28 mM, a sensitivity of 2082.57 μA mM−1 cm−2, and a detection limit of 0.7 μM. The composite further exhibits obvious stability, superior reproducibility, and excellent selectivity. This study demonstrates that NiCo2O4/rGO is a unique and material with high potential in glucose sensing.
研究领域:
材料科学
·
生物传感
·
纳米技术
✓ 已验证
产品关联
DOI
PubMed
高影响因子
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
·
2023
·
IF 10.9
Junru Yao,Jintang Zhou,Lu Lu,Feng Yang,Zhengjun Yao,Bo Ouyang,Erjun Kan,Yuxin Zuo,Renchao Che,Fan Wu
Magnetic metal absorbers exhibit remarkable microwave absorption capacity. However, their practical application is severely limited due to their susceptibility to corrosion, particularly in marine environments. To address this challenge, we propose a novel approach involving the modification and control of FeCo/rGO microwave absorbers using rare earth lanthanum (La). This strategy aims to achieve both high-performance microwave absorption and enhanced resistance to marine corrosion. In this study, we employ a La 2 O 3 modifying control strategy to refine the FeCo magnetic particles and coat them with CoFe 2 O 4 on the surface, leveraging the pinning effect of in situ generated La 2 O 3 . This process enhances the interface polarization of the absorbers, thereby improving their electromagnetic performance and marine corrosion resistance . Consequently, the La 2 O 3 modified FeCo@rGO composites exhibit broadband absorption, covering a wide frequency range of 6.11 GHz at 1.55 mm. Notably, the electromagnetic properties of the La 2 O 3 modified FeCo@rGO absorbers remain stable even after prolonged exposure to a 3.5 wt% NaCl solution, simulating marine conditions, for at least 15 days. Furthermore, we perform first-principle calculations on FeCo and FeCo O to validate the corrosion resistance of the La 2 O 3 modified FeCo@rGO composites at the atomic level. This comprehensive investigation explores the control of rare earth lanthanum modification on the size of magnetic metal particles, enabling efficient electromagnetic wave absorption and marine corrosion resistance. The results of this study provide a novel and facile strategy for the control of microwave absorbers, offering promising prospects for future research and development in this field.
研究领域:
材料科学
·
电磁学
✓ 已验证
产品关联
DOI
高影响因子
Journal of Materials Chemistry A
·
2023
·Vol. 12
·期 3
·1617-1628
·
IF 11.9
Meng Ma,Wenqin Shao,Qindan Chu,Wenting Tao,Si Chen,Yanqin Shi,Huiwen He,Yulu Zhu,Xu Wang
With the strong support of the government for emerging technology industries, electromagnetic waves have brought convenience to people's lives, but also become an undeniable new source of pollution. Therefore, it is vital to develop new high-performance electromagnetic shielding materials. Herein, we designed a well-structured asymmetrical gradient multilayer composite film by constructing a controllable electromagnetic gradient. Using cellulose nanofibers as the matrix, a layer-by-layer filtration method was used to rationally distribute FeCo@rGO and MXene fillers to build an ordered multilayer structure that provides alternating conductive and magnetic gradients. Owing to gradient absorption shielding and reflection mechanisms for electromagnetic waves within the film layer, the EMI shielding efficiency (EMI SE) of the asymmetrical gradient alternating six-layer composite film reached 45.2 dB (X-band), and the reflection coefficient was reduced to 0.71 when 20 wt% filler was added. In addition, this composite film has good thermal conductivity and mechanical properties, exhibiting thermal conductivity of 2.90 W (m−1 K−1) and tensile strength of 26.2 MPa. This strategy provides a feasible approach for designing electromagnetic shielding composite materials with adjustable electromagnetic properties and has significant practical significance in expanding the application of MXene-based composite materials.
研究领域:
材料科学
·
电磁学
·
纳米技术
✓ 已验证
产品关联
DOI
高影响因子
FIBERS AND POLYMERS
·
2021
·Vol. 23
·期 1
·254-262
·
IF 2.153
Jiang Hui-Yu,Ouyang Ze-Yu,Hu Rong,Wan Jun,Zhu Jun-Jiang
Titanium dioxide (TiO 2 ) could improve the self-cleaning performances of cotton fabric owing to its good photocatalytic performances. However, the fast recombination rate of the photogenerated electron-hole pairs and narrow photoresponse range of TiO 2 limit its wide application. In this work, Ag 2 S and reduced graphene oxider (rGO) were compounded with TiO 2 , and the composite was loaded on the surface of cotton fabric by hydrothermal method to enhance the self-cleaning performance of cotton fabric. The close contact between Ag 2 S and TiO 2 increases the light response range. Then, rGO could effectively transfer photogenerated electrons, prolong the recombination time of carriers and improve the photocatalytic efficiency. The cotton fabric was characterized by XRD, SEM, Raman and fluorescence spectra. The photocatalytic degradation of methylene blue under visible light was studied. The results showed that TiO 2 /Ag 2 S/rGO adhered uniformly on the surface of cotton fabric and had good adhesion properties. In addition, under visible light irradiation, cotton fabric has excellent photocatalytic self-cleaning performance, washing resistance and rub resistance.
研究领域:
材料科学
·
纺织工程
·
环境科学
✓ 已验证
DOI
高影响因子
PLASMA SCIENCE & TECHNOLOGY
·
2021
·Vol. 23
·期 11
·115503
·
IF 1.567
Xinghao LIU,Cheng CHENG,Zimu XU,Shuheng HU,Jie SHEN,Yan LAN,Paul K CHU
Tetracycline (TC) is an antibiotic mainly used in livestock production and respiratory infection. Traditional methods are not effective in removing TC from solution. In this study, TC was degraded by gas–liquid plasma in the presence of rGO-TiO2 in solution. The rGO-TiO2 was prepared by modified hummers and hydrothermal method. The electrical and optical properties of the gas–liquid discharge plasma were studied and the produced long-lived reactive species were analyzed by spectrophotometer. The degradation efficiency of TC was improved by 41.4% after plasma treatment for 12 min in presence of 30 mg l−1 rGO-TiO2 compared to that with plasma alone. The degradation efficiency increased with increasing discharge power, but as the initial concentration was increased from 20 to 80 mg l−1, the degradation efficiency of TC decreased. The initial pH had no significant effect on the degradation of TC. The intermediate products were determined by UV–vis spectrophotometry and ESI (+)–MS, and the degradation mechanism was analyzed. The reactive species, including O3, ·OH, and H2O2, etc., produced in the plasma/catalyst system attracted electron-rich functional groups (amino group, aromatic ring, and double bond). Therefore, the gas–liquid plasma/catalyst system could be an effective and promising method for pharmaceutical wastewater treatment in future.
研究领域:
环境科学
·
化学工程
✓ 已验证
产品关联
DOI
高影响因子
ANALYST
·
2021
·Vol. 147
·期 2
·303-311
·
IF 4.616
Chao Chen,Chenxi Wang,Pengcheng Zhao,Jin Zhang,Dechong Ma,Junjie Fei
First, the nanocomposite Au@rGO-MWCNT was synthesized by a hydrothermal method. Next, a temperature-controlled composite sensing film was prepared by composite modification of poly(2-(2-methoxyethoxy)ethyl methacrylate) (PMEO2MA) and Au@rGO-MWCNT on a glassy carbon electrode (GCE). This sensor was shown to exhibit good temperature sensitivity and reversibility to dopamine. When the testing temperature is lower than the lower critical solution temperature (LCST) of the polymer, the PMEO2MA chain is in a stretched state, which increases the distance between the Au@rGO layers and leads to the inability of MWCNTs in one layer to contact another Au@rGO layer and to low conductivity. Therefore, in this state, dopamine cannot detect an electrochemical signal, and it is termed an “off” state. When the temperature is higher than the LCST of the polymer, the PMEO2MA chain shrinks, allowing the MWCNTs to make contact with another layer of Au@rGO; the electron transfer rate of the modified film increases, and the electrochemical behavior of dopamine turns to an “on” state. Moreover, the sensor has a wide detection range (0.1 to 9.0 μM and 9.0 to 239.0 μM), and the limit of detection of dopamine is as low as 30 nM. This method has been successfully applied to the determination of dopamine in human serum samples. The on–off sensor provides a new avenue for the application of temperature-sensitive polymers.
研究领域:
生物传感
·
分析化学
·
材料科学
✓ 已验证
DOI
PubMed
高影响因子
SENSORS
·
2019
·Vol. 19
·期 6
·1281
·
IF 3.031
Qihua Sun,Zhaofeng Wu,Haiming Duan,Dianzeng Jia
Triacetone triperoxide (TATP) is a self-made explosive synthesized from the commonly used chemical acetone (C3H6O) and hydrogen peroxide (H2O2). As C3H6O and H2O2are the precursors of TATP, their detection is very important due to the high risk of the presence of TATP. In order to detect the precursors of TATP effectively, hierarchical molybdenum disulfide/reduced graphene oxide (MoS2/RGO) composites were synthesized by a hydrothermal method, using two-dimensional reduced graphene oxide (RGO) as template. The effects of the ratio of RGO to raw materials for the synthesis of MoS2on the morphology, structure, and gas sensing properties of the MoS2/RGO composites were studied. It was found that after optimization, the response to 50 ppm of H2O2vapor was increased from 29.0% to 373.1%, achieving an increase of about 12 times. Meanwhile, all three sensors based on MoS2/RGO composites exhibited excellent anti-interference performance to ozone with strong oxidation. Furthermore, three sensors based on MoS2/RGO composites were fabricated into a simple sensor array, realizing discriminative detection of three target analytes in 14.5 s at room temperature. This work shows that the synergistic effect between two-dimensional RGO and MoS2provides new possibilities for the development of high performance sensors.Keywords:(TATP) precursors;MoS2/RGO composites;sensor arrays;synergistic effect
研究领域:
化学工程
·
材料科学
·
传感技术
✓ 已验证
产品关联
DOI
PubMed
高影响因子
SENSORS AND ACTUATORS B-CHEMICAL
·
2023
·
IF 8.4
Haineng Bai,Cheng Feng,Hui Guo,Xiaoli Li,Weifeng Liu,Yamin Feng,Kuili Liu,Dunjun Chen,Youdou Zheng,Fuqiang Guo
Monitoring and reducing NO 2 pollution at room temperature is indispensable for human survival. Thus, we propose a light-activated route (UV light, 100 mW/cm 2 ) to realize a high-performance NO 2 detection based on CuO/rGO gas sensor. The CuO/rGO sensor under UV light illumination exhibits a high response of 22.18–100 ppm NO 2 at 23 ℃, which is approximately 1.36 times of the CuO/rGO sensor and 2.31 times of the CuO sensor under dark, respectively. Meanwhile, under UV light illumination, the CuO/rGO sensor has a fast response/recovery speed of 10.9/30.9 s to 20 ppm NO 2 at 23 ℃, which is obviously better than that under dark. Moreover, the light-activated CuO/rGO sensor has excellent repeatability, selectivity, ultra-low detection limit (50 ppb) and long-term stability. The significantly appealing gas-sensing performance of CuO/rGO sensor is mainly ascribed to the mesoporous structure, high specific surface area and plentiful oxygen vacancy of CuO/rGO nanocomposites . More attractively, the photo-generated carriers and formed heterojunction also greatly improve the carrier migration in the context of the NO 2 /CuO/rGO interaction, enhancing the gas-sensing performance of gas sensor. Our work will provide insight in utilizing light illumination to realize ultrasensitive and room-temperature detection of ppb-level NO 2 gas.
研究领域:
材料科学
·
环境科学
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF HAZARDOUS MATERIALS
·
2018
·
IF 6.434
Hailong Wang,Quanqin Hu,Yuan Meng,Zier Jin,Zilin Fang,Qinrui Fu,Wenhua Gao,Liang Xu,Yibing Song,Fushen Lu
Reduced graphite oxide (rGO) was incorporated into a metal organic framework (MOF) MIL-101(Cr) for the modification of carbon paste electrode. Taking advantages of the large surface area of MOF and the electrical conductivity of rGO, the resulted electrodes exhibited high sensitivity and reliability in the simultaneous electrochemical identification and quantification of catechol (CC) and hydroquinone (HQ). Specifically, in the mixture solution of catechol and hydroquinone (constant concentration of an analyte), the linear response ranges for catechol and hydroquinone were 10–1400 μM and 4–1000 μM, and detection limits were 4 μM and 0.66 μM (S/N = 3) for individual catechol and hydroquinone, respectively. Therefore, the relatively easy fabrication of modified CPE and its fascinating reliability towards HQ and CC detection may simulate more research interest in the applications of MIL-101(Cr)-rGO composites for electrochemical sensors.
研究领域:
分析化学
·
材料科学
·
环境科学
✓ 已验证
DOI
高影响因子
CHEMICAL ENGINEERING JOURNAL
·
2024
·
IF 13.3
Dinh-Trinh Tran,Thi-Phuong-Thao Vu,Santi Kongmany
In this study, ZnFe 2 O 4 , BiVO 4 , and ZnFe 2 O 4 /BiVO 4 /rGO materials were synthesized using the hydrothermal method in mild conditions to study the oxytetracycline (OTC) degradation process. The results on surface morphology, functional group, structure, and optical and electrochemical characteristics revealed that ZnFe 2 O 4 /BiVO 4 /rGO were successfully prepared with high purity and good distribution of chemical elements. The impact of different parameters like pH, catalyst load, reaction time, initial OTC concentration, and the presence of ozone-nanobubbles on the OTC degradation efficiency was systematically examined to obtain optimal treatment conditions. Synergic effects between ozone-nanobubbles and ZnFe 2 O 4 /BiVO 4 /rGO heterojunction led to an enhancement of over 20 % of OTC degradation yield. The OTC degradation reached 96.3 % within 100 min at optimal conditions (pH 7.0, [Cat.] = 0.5 g/L, and [OTC] = 20 mg/L). The combination of ZnFe 2 O 4 and BiVO 4 allowed to benefit from the generation of both effective electrons and holes, which enhanced the generation rate of both superoxide and hydroxyl radicals responsible for degrading the pollutant in water while rGO sheets contributed to slowing down the recombination rate between electrons and holes and improving the photocatalytic activities of the ZnFe 2 O 4 /BiVO 4 /rGO. Liquid chromatography-mass spectrometry (LC-MS) analyses were deployed to figure out intermediate substances and possible degradation pathways of the OTC degradation process. The ZnFe 2 O 4 /BiVO 4 /rGO heterojunction exhibited a pretty good durability and stability, and was easily recovered with the aid of a magnet. The toxicity of the by-products was significantly declined compared to the OTC antibiotic.
研究领域:
环境科学
·
材料科学
·
微生物学
✓ 已验证
产品关联
DOI
高影响因子