JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
·
2025
·
IF 6.2
Jinyu Wu,Zhongyan Wang,Kelan Zhang,Ze Wu,Lingyi Meng,Heng Chen,Xiaoxia Hu,Xiaohui Ma,Anran Guo
For continuing to explore new high-entropy materials, the first high-entropy ilmenite-phase titanate, (Mg,Co,Ni,Zn)TiO 3 , is synthesized in this work, further introducing a new crystal structure type for high-entropy ceramics. The uniform chemical composition and typical ilmenite-phase structure of high-entropy (Mg,Co,Ni,Zn)TiO 3 are verified by XRD, SEM, TEM, EDS, and XPS. Homogeneous element distribution and magnetically-coupled atomic arrangement are further performed using Rietveld refinement, Raman spectral fitting, and high-resolution STEM. On this basis, complementary density functional theory simulation with Hubbard correction (DFT + U) is conducted to reveal the band structure and a 2.529 eV bandgap of high-entropy (Mg,Co,Ni,Zn)TiO 3 , thereby enhancing the potential for high emissivity and electronic applications. Excellent thermal stability at 1000–1200 °C, a low thermal conductivity of 2.365 W·m⁻¹·K⁻¹ at room temperature, a high hemispherical emissivity of 0.93 within the 3–14 μm wavelength range, and a low dielectric constant of 22.23 are also demonstrated.
✓ 已验证
产品关联
DOI
高影响因子
Materials Today Communications
·
2024
·
IF 3.7
Yang Liu,Run Liu,Wenxian Nie,Leiting Yu,Shaoyuan Lyu,Qi Han,Yun Zhao,Minfang Chen
In this study, a composite coating of polycaprolactone layer and polydopamine-cyclodextrin (β-CD)/naringenin (NG) was prepared on the surface of a micro-arc oxidized (MAO) pretreated magnesium alloy by a two-step method. The findings demonstrate that the composite coating exhibits favorable corrosion resistance, biocompatibility, photo-thermal antimicrobial, and bone-enhancing characteristics. Compared with the MAO coating, the corrosion rate of the composite coating was significantly reduced from about 0.087 mm/y to 0.066 mm/y. The antimicrobial efficiency of the coating against Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) under 808 nm laser irradiation was found to reach 93 % and 99 %, respectively. Furthermore, in vitro cytotoxicity assays, dead and live cell staining, and immunoblotting analysis showed that the coating exhibited favorable biocompatibility and osteogenic activity. This novel coating may have good application prospects in the treatment of osteoporosis-related fractures.
✓ 已验证
DOI
高影响因子
Journal of Energy Storage
·
2022
·
IF 8.907
Hui Wang,Enda Ci,Xiaoqing Li,Ying Zhang,Zhenying Zhang,Jianqiang Li
A new eutectic mixture phase change material containing magnesium nitrate hexahydrate and lithium nitrate has been successfully prepared, which can be applied in the field of residential radiator heating due to the suitable phase change temperature and high latent heat. Further, by physical blending magnesium nitrate hexahydrate/lithium nitrate eutectic mixtures and expanded graphite, the new composites were prepared. The crystalline structure, thermal properties, corrosion performance of eutectic phase change materials were systematically measured. The results showed that the best eutectic mixtures had a phase change temperature of 72.35 °C and latent heat of 170.32 kJ/kg, with a little supercooling degree. The thermal conductivity was effectively improved by adding expanded graphite. Meanwhile, corrosion tests suggested aluminum and stainless steel 304 could be the preferred choices as the container. Overall, the prepared eutectic composite materials with superior performances could be a promising candidate for the residential radiator heating field.
✓ 已验证
DOI
高影响因子
CERAMICS INTERNATIONAL
·
2022
·
IF 5.532
Yan Zhao,Pengjun Zhao,Qing Zhao,Donglin He,Wenwen Kong,Bing Wu,Aimin Chang
Herein, Mg–Al–Si–Ba–O-based glass ceramics were studied as potential candidates to protect Mn–Co–Ni–O-based negative temperature coefficient (NTC) thermistors at high temperatures such as 900 °C. The ceramics were prepared in three glass formulations (1#: 15MgO–15Al 2 O 3 -44.7SiO 2 –25BaO, 2#: 17MgO–17Al 2 O 3 –41SiO 2 –25BaO and 3#: 17MgO–17Al 2 O 3 –41SiO 2 –20BaO–5Y 2 O 3 (in mol%)) and their glass-transition temperatures ( T g ) were determined using the differential scanning calorimetry (DSC) method. Scanning electronic microscopy (SEM) and X-ray diffraction (XRD) were used to characterize the parent glasses and glass-ceramic coatings. The sealing effects of the glass ceramics were examined by conducting an insulation test. The glass-ceramic sealing structures were subjected to 1000 thermal shock cycles at temperatures varying from room temperature to 900 °C. Notably, the sealing structure of glass-ceramic coating 1# was compact at a T g of 760.9 °C. The glass-ceramic coatings effectively maintained the NTC properties of the sensitive ceramics in all three formulations. Interestingly, the glass-ceramic coating 3# containing Y 2 O 3 demonstrated an increase in electrical resistance. Both the NTC thermistors coated with 1# and 2# glass formulations successfully passed 1000 thermal shock cycles without visible failures, and their resistance change ratios were well below the requisite 20%.
✓ 已验证
DOI
高影响因子
Journal of Materials Chemistry A
·
2017
·Vol. 5
·期 20
·9723-9732
·
IF 8.867
Jiaguang Zheng,Xuezhang Xiao,Liuting Zhang,Shouquan Li,Hongwei Ge,Lixin Chen
A remarkable improvement in the hydrogen desorption performance of Mg(BH4)2–NaBH4 eutectic composite is achieved by simply ball-milling with fluorographene (FG). It is found that the desorption temperature of Mg(BH4)2–NaBH4 (∼200 °C) is still too high and liquid phase appears during dehydrogenation. Particularly, the novel bowl-like 3D Mg(BH4)2–NaBH4–FG composite can be formed after ball-milling. The novel Mg(BH4)2–NaBH4–FG exhibits a low dehydrogenation temperature of 114.9 °C with 6.9 wt% of pure hydrogen in seconds. In-depth investigations show that such greatly improved hydrogen desorption properties of the Mg(BH4)2–NaBH4–FG composite could be ascribed to both the “novel bowl-like 3D structure” with large specific surface area and the “reactant destabilized modification” owing to the decrease of the reaction enthalpy caused by the formation of NaMgF3. This finding provides a facile preparation of complex borohydride composites with low dehydrogenation temperature and fast rate, which accelerates its practical application in fuel cells.
✓ 已验证
DOI
高影响因子
JOURNAL OF ALLOYS AND COMPOUNDS
·
2018
·
IF 3.779
Yao Lu,Carlos Alberto López,Jie Wang,José Antonio Alonso,Chunwen Sun
Na 0.5 Bi 0.5 TiO 3 (NBT) and its acceptor-doped perovskites , as lead-free piezoelectric materials before, have been found to be excellent oxygen-ion conductors with potential applications in intermediate-temperature solid oxide fuel cells (SOFCs). Among them, the Bi deficient and B-site Mg doped sodium bismuth titanate (Na 0.5 Bi 0.49 Ti 0.98 Mg 0.02 O 2.965 , NBTM) exhibits a remarkable oxygen ionic conductivity . Here, we report a structural analysis on NBT and NBTM ceramics using high-temperature in situ neutron diffraction (NPD) to gain insight into the effects of Mg doping on ionic conductivity and structure. Both perovskite oxides exhibit two consecutive phase transformations from R 3 c to P 4 bm at ∼400 °C and from P 4 bm to Pm 3 ¯ m at ∼600 °C. The effects of Bi deficiency and Mg substitution on oxygen vacancy concentration and ion displacements are revealed. In addition, a NBTM supported single cell consisting of Ag-NBTM cathode and Ni-NBTM anode is fabricated to evaluate the possibility of its application in intermediate-temperature SOFCs. The structural stability of NBTM is still a major concern that hinders its utilization at high temperature and under reducing atmosphere.
✓ 已验证
DOI
高影响因子
JOURNAL OF BIOMATERIALS APPLICATIONS
·
2025
·
IF 2.5
Jian Gu,Shuangjian He,Peng Zhang,Long Zhou
Infected bone defects are characterised by inadequate local blood supply and the formation of bacterial biofilms, which impede bone tissue regeneration and repair, presenting a significant clinical challenge. In this study, we developed a bifunctional scaffold combining near-infrared (NIR)-responsive antibacterial activity with osteogenic properties by co-electrospinning photothermally active copper hydroxyphosphate (Cu2(OH)PO4, CuHP) and osteogenic magnesium-calcium phosphate (Mg-CaP) into poly (L-lactic acid) (PLLA) membranes. Near-infrared (NIR) irradiation activates the photothermal response of CuHP in nanofiber membrane scaffolds, effectively killing bacteria through photothermal therapy (PTT), while the released Mg-CaP synergistically promotes osteogenesis. Animal studies have revealed that the scaffold effectively inhibit infections while accelerating bone healing, offering a promising strategy for infected bone defects.
✓ 已验证
DOI
PubMed
高影响因子
DIAMOND AND RELATED MATERIALS
·
2022
·
IF 3.806
L.L. Xie,J.H. Chu,X.J. Li,D.N. Zou,L.B. Tong
Epoxy resin (EP) coating has high hydrophilicity and poor long-term corrosion resistance . In order to improve its protection ability, an EP-graphene oxide (GO)/SiO 2 multifunctional coating is fabricated on Mg-Zn-Ca alloy in this study, through a spin/spray assisted self-assembly technique. The morphologies and microstructures of the coated samples were observed using scanning electron microscopy (SEM), Fourier infrared spectrometer (FTIR) and atomic force microscope (AFM). Hydrophobicity and self-cleaning property of the composite coating were tested by an optical contact angle meter and black graphite powders . The stability of the superhydrophobic surface was tested by rubbing with sandpaper and immersing in corrosion solution. The corrosion resistance of coated samples was tested in 3.5 % NaCl solution using electrochemical impedance spectroscopy (EIS). The GO sheets are uniformly dispersed in EP coating. EP-GO acts as a dense bottom layer, effectively promoting its adhesion with the superhydrophobic SiO 2 coating, and the water contact angle (WCA) values range from 158° to 168°. After stability testing, the WCA value of the superhydrophobic coating remains at a high level (115°–155°). The R ct of this composite coating was remarkably increased to 1.0 × 10 22 Ω/cm 2 , implying that the corrosion resistance was improved by eighteen orders of magnitude compared to bare substrate. These results show that the combination of the labyrinth effect and the hydrophobic surface extend the corrosion path and reduce the contact area of the corrosion solution with the coating, which strengthens the barrier effect of the composite coating. The composite coating exhibits superior corrosion resistance durability and self-cleaning property.
✓ 已验证
DOI
高影响因子
ACS Earth and Space Chemistry
·
2025
·
IF 2.9
Qi Tao,Yonglei Zhang,Tianqi Zhang,Xiaorong Qin,Binglong Ye,Hongping He,Sridhar Komarneni
Over the past decade, remote sensing exploration has revealed widespread detection of clay minerals in Noachian terrains (>3.7 Ga) on Mars, suggesting a period of active near-surface water–rock interaction. The in-depth characterization of the crystal structure and chemistry of laboratory-synthesized smectite minerals with varying compositions offers a unique perspective to further constrain their formation mechanism, environmental conditions, and the climate of early Mars. This study synthesized smectites with varying Fe/Mg ratios to compare their near-infrared (NIR) spectral characteristics with those of representative areas on Mars. The study revealed that the characteristic metal–OH (M–OH) band in the range of 2270–2320 nm shifted toward longer wavelengths as the octahedral Fe3+ content decreased. When the octahedral Fe/Mg ratio was close to 1, the position of M–OH was similar to that of Mg-smectite (saponite), indicating that although the M–OH band of smectite is located at ca. 2308–2312 nm, it may still contain a significant amount of octahedral Fe3+. This suggests that there are likely still many Fe-smectites in Mg-rich smectite outcrops (ca. 20% as in the literature) on the Martian surface. Furthermore, correlation analysis between the smectite layer stacking order index (V/P) and the second-order derivative band intensity ratio (Deriv2 ratio) showed that when the Deriv2 ratio is small (generally <8), smectite has a relatively high degree of layer stacking order. When the Deriv2 ratio is >10 and tends toward infinity (+∞), the layer stacking order of smectite is very low. The above results suggest that the crystal chemical characteristics of smectites should be carefully studied when analyzing the mineral composition of the Mars surface using remote sensing or in situ NIR spectra. Smectites on Mars generally exhibit a high layer stacking order, indicating the presence of a relatively long-term warm and humid climate in Martian history. However, later alteration processes can significantly reduce their crystallinity.
✓ 已验证
产品关联
DOI
高影响因子
COLLOIDS AND SURFACES B-BIOINTERFACES
·
2025
·
IF 5.6
Xin Zhao,Jingjing Jiao,Man Ao,Lin Huang,Peng Xu,Yan Shi,Jiao-jing Shao,Yuanlong Guo,Haibo Xie,Long Li,Qiuyue Ding,Zhu Chen
Bacterial infection, excessive inflammation, and insufficient tissue remodeling capacity are major factors to delayed or impaired wound healing. This study synthesized Mg-doped bioactive glass (MBG) using the sol-gel method. Subsequently, based on polycaprolactone (PCL), MBG and tea polyphenols (TP), a Janus wound dressing with an enhanced hydrophilic and antibacterial outer layer of PCL-TP (PT) and a hydrophobicity-preserved and tissue generation-promoting inner layer of PCL-MBG (PB) was further fabricated using a sequential electrospinning method. This design endowed the dressing with directional fluid transport property to effectively prevent tissue adhesion and exudate infiltration. In vitro drug release results demonstrated that ions such as Si, Mg, Ca, and P were sustainably released up to 5 days at least, while TP could be slowly released for over 7 days. The fibrous membrane loaded with TP showed significant inhibition against S. aureus and E. coli, with increasing antibacterial activity as the increase of TP content. The cytological evaluation confirmed that dressings incorporating with MBG and TP did not exhibit cytotoxicity but significantly promoted cell proliferation. The PB/PT Janus dressing demonstrated an apparent repair area exceeding 99 % in animal experiments, along with a significantly higher number of new hair follicles and collagen ratio compared to the blank and PCL groups. These results indicate the potential of this Janus wound dressing in effectively promoting wound healing.
✓ 已验证
产品关联
DOI
PubMed
高影响因子
Biomaterials Science
·
2018
·Vol. 6
·期 5
·1227-1237
·
IF 5.831
Qianwen Li,Donghui Wang,Jiajun Qiu,Feng Peng,Xuanyong Liu
Hard tissue implant materials which can cause a suitable alkaline microenvironment are thought to be beneficial for stimulating osteoblast differentiation while suppressing osteoclast generation. To make the local pH around the interface between materials and cells controllable, we prepared a series of Mg–Fe layered double hydroxide (LDH) films on acid-etched pure titanium surfaces via hydrothermal treatment. By adjusting the Mg/Fe proportion ratio, the interlayer spacing of Mg–Fe LDHs was regulated, making their OH− exchange abilities adjustable, and this ultimately resulted in a microenvironment with a controllable pH value. In vitro experiments demonstrated that the Mg–Fe LDH film-modified titanium surface possessed good biocompatibility and osteogenic activity, especially the Mg–Fe LDH film with Mg/Fe proportion ratio of 4, which could form a suitable alkaline microenvironment for the growth and osteogenetic differentiation of stem cells. These results demonstrate the potential application of the prepared Mg–Fe LDH films in enhancing the osteogenesis of implant materials while providing a new way into the design of controllable alkaline environment.
✓ 已验证
DOI
PubMed
高影响因子
Frontiers in Materials
·
2022
·
IF 3.985
Feng Yashan,Chang Lei,Zhu Shijie,Yang Yongxin,Wei Baoli,Lv Meng,Wang Jun,Guan Shaokang
The uncontrollable rapid degradation rate of the Mg alloy substrate limited its clinical application, and implant-associated infections have been reported to be the main reason for the secondary surgery of orthopedic implantation. The aim of this study was to produce a multifunctional coating on magnesium-based alloys that have improved corrosion resistance, bioactivity, and antibacterial properties through the preparation of polyelectrolytic multilayers (PEMs) consisting of chitosan (CS) and sodium hyaluronate (HA) on silane-modified strontium-substituted hydroxyapatite (hereafter referred to as Bil (SH + CS)/SrHA). The multifunctional coatings were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and X-ray photoelectron spectroscopy (XPS). The results showed the polyelectrolyte complex SH/CS layer to be uniformly and tightly attached on to the surface of silane-treated SrHA. At the same time, a potentiodynamic polarization test and hydrogen evolution test showed the Bil (SH + CS)/SrHA coatings to exhibit superior corrosion resistance than bulk Mg-based alloys. The results of the cell–surface interactions revealed Bil (SH + CS)/SrHA coatings to be in favor of cell initial adhesion and more beneficial to the proliferation and growth of cells with the processing of co-culture. In addition, antibacterial tests demonstrated the strong bactericidal effect of Bil (SH + CS)/SrHA coatings against both Escherichia coli (E. coli) and Staphylococcus (S. aureus), suggesting that Bil (SH + CS)/SrHA coatings can successfully achieve multifunctionality with enhanced corrosion resistance, biocompatibility, and antibacterial properties.
✓ 已验证
DOI
高影响因子