CERAMICS INTERNATIONAL
·
2023
·Vol. 49
·期 11
·18776-18785
·
IF 5.2
Jiaxu Cheng,Siwei Jiang,Jiahong Fan,Jun Yao,Ning Du,Xue Li,Ding Wang,Peng Dong,Zhongren Zhou,Yingjie Zhang
Molten salt electrolytic synthesis of silicon is identified as a potential industry method due to its thorough deoxidization of oxide and short-flow synthetic progress. However, figuring out a more efficient and sustainable strategy for the increase of the reduction process as well as the control of product morphology still needs endless research. In this study, benefiting from the high electrical conductivity of metallic silver and the easy separation of silver from silver-silicon alloys during the electrolysis of SiO 2 , metallic silver was introduced to electric-catalyze the production of silicon. Firstly, metallic silver was introduced into the silica matrix by a simple silver mirror reaction. Secondly, the mixed Ag\SiO 2 precursor was located at the cathode for molten salt electrolysis . Finally, silicon nanowires were herein achieved in molten NaCl–CaCl 2 . Mechanisms of metal Ag played during the electric-polarization process of silica and the electrochemical nucleation of silicon were further analyzed by X-ray diffraction (XRD), Scanning Electron Microscope (SEM), Field-Emission Scanning Electron Microscope (FESEM), Transmission Electron Microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and Raman spectra . The results demonstrate that Ag helps construct Si nanowires via a classic Ag-Si binary alloy-droplet process and provided quantitative guidance for the large-yield production of silicon nanowires via adding 0.08–0.17 g Ag versus 1 g SiO 2 , controlling the temperature at 850–900 °C and electrolysis voltage at 2.6–2.8 V (2.6V at first 1 h and 2.8V at last 5 h). The synthesized silicon nanowires present two types of linear structures based on two three-phase interlines (3PIs) models and a streamed long-straight nanowire is observed.
研究领域:
材料科学
·
纳米科技
·
电化学
·
无机化学
·
能源材料
·
半导体材料
✓ 已验证
DOI
高影响因子
ZEITSCHRIFT FUR ANORGANISCHE UND ALLGEMEINE CHEMIE
·
2021
·Vol. 647
·期 6
·681-685
·
IF 1.492
Xieyang Wang,Zhen Dong,Rui Yang,Shengren Zhou,Zhiwen Ye
Two energetic salts of cyclo-N 5 − , O-methylisoure pentazolate ( 1 ) and guanidinoacetic acid pentazolate ( 2 ), were synthesized by metathesis reaction. All the energetic cyclo-N 5 − salts were characterized by single-crystal XRD, IR spectroscopy, 1 H and 13 C multinuclear NMR spectroscopy, thermal analysis (DSC) and elemental analysis. They exhibit good thermal stability with decomposition temperatures of more than 100 °C and they are in excellent agreement with those reported non-metallic salts. Salt 1 also exhibits strong π-π interactions. The standard enthalpies of formation and detonation performances of these salts were calculated using Gaussian 09 and EXPLO5 v6.01 programs. The detonation velocities of compound 1 and 2 are both about 7400 m s −1 and these two salts exhibit low mechanical sensitivity (IS>23 J, FS>220 N). Therefore, in this work, the synthesis of the new pentazolate salts enriches the cyclo-pentazolate salts system, which is conducive to the exploration of more heat-resistant and higher detonation velocities pentazolate salts.
研究领域:
无机化学
·
含能材料
·
热分析
·
结构化学
✓ 已验证
DOI
高影响因子
CATALYSIS COMMUNICATIONS
·
2011
·Vol. 15
·期 1
·52-55
·
IF 2.827
Ben Qi,Lan-Lan Lou,Kai Yu,Wenyue Bian,Shuangxi Liu
A series of manganese oxides (MnO, Mn 3 O 4 , Mn 2 O 3 and MnO 2 ) were prepared and firstly applied as heterogeneous catalysts for the liquid phase epoxidation of alkenes with 30% H 2 O 2 in bicarbonate solution. Under our experimental conditions, MnO exhibited superior activity for the conversion of styrene to achieve ca. 100% with 92.4% selectivity of epoxide, compared to the other three manganese oxides as well as other metal oxides. Furthermore, recycling studies showed the good recyclability of MnO as a heterogeneous catalyst, which did not lose the catalytic activity after four reuses appreciably.
研究领域:
催化化学
·
有机合成
·
材料化学
·
绿色化学
·
工业化学
✓ 已验证
DOI
高影响因子
MICROCHIMICA ACTA
·
2010
·Vol. 171
·期 3
·385-392
·
IF 2.648
Yin Huanshun,Zhou Yunlei,Liu Tao,Cui Lin,Ai Shiyun,Qiu Yanyan,Zhu Lusheng
An amperometric biosensor for nitrite was prepared by immobilizing cytochrome c (Cyt c) on a gold electrode that was modified with Nafion and a Cu-Mg-Al layered double hydroxide (Cu-LDH). The Cu-LDH was characterized by Fourier transform infrared spectroscopy and powder X-ray diffraction. The UV-visible spectrum suggests that Cyt c retains its native conformation in the modified film. The direct electrochemical investigation indicated that the composite film represents a good platform for the immobilization of Cyt c as well as an excellent promoter for the electron transfer between Cyt c and the gold electrode. Moreover, the biosensor showed a remarkable bioelectrocatalytic activity for the oxidation of nitrite with a linear range from 0.75 to 123 μM. The detection limit is 2 × 10 −7 M (S/ N = 3). The biosensor was successfully applied to the determination of nitrite in food samples.
研究领域:
生物分析化学
·
电化学传感
·
食品分析
·
生物传感器
·
分子诊断
✓ 已验证
DOI
高影响因子
ELECTROCHIMICA ACTA
·
2019
·
IF 5.383
Bin Xiao,Wen-hai Zhang,Peng-bo Wang,Lin-bo Tang,Chang-sheng An,Zhen-jiang He,Hui Tong,Jun-chao Zheng,Bo Wang
Phosphate-based polyanion-structured materials have attracted considerable attention as anode materials in lithium-/sodium-ion batteries due to their stable crystal structure, affordability, and environmental friendliness. V 2 (PO 4 )O was encapsulated into crumpled nitrogen-doped graphene (VPO@N-G) through a facile spray-drying method in which VPO particles were completely encapsulated by N-doped graphene. For the first time, VPO@N-G was explored as an anode material for sodium-ion batteries. The Na + storage behavior of VPO@N-G was systematically investigated at the voltage range of 0.01–3.0 V (versus Na/Na + ). Results indicated that the VPO@N-G anode can deliver a highly reversible discharge capacity of 539 mAh g −1 at 0.05 A g −1 and achieve a highly reversible discharge capacity of 235.9 mAh g −1 even at a high current density of 10 A g −1 . Thus, VPO@N-G can be applied as a high-rate anode material for sodium-ion batteries.
研究领域:
材料科学
·
电化学
·
能源存储
·
纳米复合材料
·
无机功能材料
✓ 已验证
DOI
高影响因子
JOURNAL OF RARE EARTHS
·
2015
·Vol. 33
·期 9
·927-932
·
IF 1.261
Hailong PENG,Qiangsheng GAO,Lili MENG,Lixia ZHANG,Qi PANG,Lifang LIANG
Ca 12 Al 14 O 32 F 2 :Eu 3+ red phosphors were prepared by the sol-gel method with CF 3 COOH as the fluorine source. X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectra, and photoluminescence spectra, as well as thermogravimetric and differential thermal analysis were utilized to characterize the samples. All the samples were single phase with a cubic structure. The as-obtained Ca 12 Al 14 O 32 F 2 :Eu 3+ red phosphors consisted of nanoparticles with sizes of approximately 40–100 nm. Under the excitation of UV light, Ca 12 Al 14 O 32 F 2 :Eu 3+ exhibited the characteristic emissions of Eu 3+ , and the effect of annealing temperature, annealing time, and CF 3 COOH and Eu 3+ concentrations on the luminescence intensity were discussed in detail.
研究领域:
材料科学
·
无机化学
·
发光材料
·
纳米材料
·
固体化学
✓ 已验证
DOI
高影响因子
JOM
·
2019
·Vol. 72
·期 6
·2245-2249
·
IF 2.305
Zhang Yannan,Zhang Yingjie,Li Xue,Liu Jiaming,Zhang Mingyu,Yang Xi,Huang Mengyang,Xu Mingli,Dong Peng,Zhou Zhongren
The molten salt electrolytic method was introduced to prepare metallic silicon that simply utilizes SiO 2 powder as the raw material and equimolar CaCl 2 -NaCl as the electrolyte under 1.8 V current at 700°C for 5 h.
The electrochemically synthesized silicon was in the form of nanowire structures with average sizes of 90 nm in diameter and over 1 μm in length. The current efficiency and specific energy consumption of producing silicon nanowires were calculated to be 79.2% and 8.703 kWh/kg, respectively. Benefiting from the synthesized nanowire structure, the silicon anode exhibited a high initial discharge-specific capacity of 3348.1 mAh/g with an initial coulombic efficiency of 85.2%.
The present research provides a straightforward idea to show the feasibility of synthesizing silicon-based material by the molten salt electrolytic method and to introduce the application of synthesized silicon nanowires to lithium-ion battery systems.
研究领域:
材料科学
·
电化学
·
纳米科技
·
能源存储
·
无机合成
✓ 已验证
DOI
高影响因子
JOURNAL OF MEMBRANE SCIENCE
·
2018
·
IF 6.578
Shaosuo Bing,Jiaqian Wang,Hao Xu,Yanyan Zhao,Yong Zhou,Lin Zhang,Congjie Gao,Li’an Hou
Polyamide (PA) thin-film composite (TFC) reverse osmosis membrane is widely used for desalination , but the selectivity-permeability trade-off and oxidation are two major restrictions on the membrane application. By modifying PA TFC membrane with potassium persulfate (K 2 S 2 O 8 ), we overcame the trade-off relation (the water flux and salt rejection increased by 43.2% and 0.2%, respectively) and improved the chlorine resistance. The modification was demonstrated to be a combination of the interfacial crosslinking between PA layer and polysulfone support with the surficial oxidation of PA layer. The dense crosslinked interface enabled the membrane with higher solute rejection, better chlorine tolerance and long-term stability. Meanwhile, the thinner PA layer contributed to the increase of membrane permeability. Furthermore, the modification method has the application potential in high-performance membrane fabrication in terms of simplicity and high efficiency.
研究领域:
材料科学
·
膜分离技术
·
高分子化学
·
环境工程
·
水处理
✓ 已验证
DOI
高影响因子
JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
·
2014
·Vol. 26
·期 2
·884-890
·
IF 1.966
Li Rui,Wang Yan-ze,Mao Zhi-yong,Wang Da-Jian
A remote phosphor coating by using Sr 3 (Al,Si)(O, F) 5 :Ce 3+ (SASF:Ce 3+ ) on glass substrate was prepared by a simple and convenient screen printing method. The crystalline phase and the distribution of SASF:Ce 3+ crystals in coating were investigated by XRD and SEM, respectively. The scattering light and absorption light properties of remote phosphor coating with different thicknesses were discussed through Lambert–Beer’s law. The relationship between luminous efficiency and absorption coefficient was demonstrated. White light emitting diode prototype fabricated with blue chip and the prepared patterned SASF:Ce 3+ remote phosphor in this work showed excellent performances, opening a cost-effective process to generate planar white light.
研究领域:
材料科学
·
光学工程
·
发光材料
·
固态照明
·
功能涂层
✓ 已验证
DOI
高影响因子
JOURNAL OF HAZARDOUS MATERIALS
·
2021
·
IF 10.588
Xuefeng Liu,Shijie You,Nanqi Ren,Hao Zhou,Jinna Zhang
This study reports the development of complete solar-driven dual-photoelectrode fuel cell (PFC) based on WO 3 photoanode and Cu 2 O photocathode with peroxymonosulfate (PMS) serving as cathodic electron acceptor . As indicated by photoelectrochemical measurements, the PMS was able to improve thermodynamic properties of photocathode, achieving an increased open circuit potential from 0.42 V to 0.65 V vs standard hydrogen electrode (SHE). Under simulated sunlight irradiation (~100 mW cm −2 ), the maximum power density of 0.12 mW cm −2 could be obtained at current density of 0.34 mA cm −2 , which was 8.57 times of that produced by PFC without PMS (0.014 mW cm −2 ). Correspondingly, adding PMS (1.0 mM) increased overall removal efficiency of 4-chlorophenol (4-CP) from 39.8% to 96.8%, accounting for the first-order kinetic constant ( k =0.056 min −1 ) being 6.67 times of that in the absence of PMS ( k =0.0084 min −1 ). Radical quenching and electron spin-resonance (ESR) results suggested the contribution of free radicals (•OH and SO 4 •- ) and non-radical pathway associated with direct activation of PMS by Cu 2 O photocathode. Fourier transformed infrared (FTIR) analysis confirmed the strong non-radical interaction between Cu 2 O photocathode and PMS, resulting in 4-CP removal via activation of PMS by surface complex on Cu 2 O. The proof-in-concept complete solar-driven dual-photoelectrode fuel cell may offer an effective manner to realize water purification and power generation, making wastewater treatment more economical and more sustainable.
研究领域:
环境科学
·
光催化
·
能源材料
·
电化学
·
水处理技术
·
可持续能源
✓ 已验证
DOI
高影响因子
JOURNAL OF ALLOYS AND COMPOUNDS
·
2021
·
IF 5.316
Kaitong Liu,Jian Han,Fuming Li,Congcong Jin,Zhihua Yang,Miriding Mutailipu,Shilie Pan
A case of hydrous borate with the formula of Ba 2 B 13 O 19 (OH) 5 ·5H 2 O was synthesized by the traditional hydrothermal method . It crystallizes in the chiral P 1 space group and has a unique two-dimensional 2 [B 13 O 19 (OH) 5 ] ∞ layer that is constructed by the hydrogen involved [B 13 O 22 (OH) 5 ] fundamental building blocks (FBBs). The Ba atoms and H 2 O molecules are filled in the three-dimensional pore constructed by the 2 [B 13 O 19 (OH) 5 ] ∞ layer. Interestingly, Ba 2 B 13 O 19 (OH) 5 ·5H 2 O is the first case of hydrous borates that has the above rare [B 13 O 22 (OH) 5 ] FBB and 2 [B 13 O 19 (OH) 5 ] ∞ layer, which enriching the structural chemistry of borate system. The diffuse reflection spectrum result shows that the ultraviolet (UV) cutoff edge of Ba 2 B 13 O 19 (OH) 5 ·5H 2 O is below 200 nm. Its second harmonic generation (SHG) response is approximately 1.0 times that of potassium dihydrogen phosphate at the 1064 nm fundamental wavelength and it is also phase-matchable. Both results indicate that the title compound is a nonlinear optical crystal for UV spectral region. Theoretical simulation calculation shows that the occupied VE states are mainly contributed by the O-2p orbitals, and therefore [B 13 O 22 (OH) 5 ] groups are the main sources of SHG effects.
研究领域:
无机化学
·
材料科学
·
晶体工程
·
光学材料
·
固体化学
✓ 已验证
DOI
高影响因子
OPTICAL MATERIALS
·
2019
·
IF 2.687
Jiang Wu,Haowen Bai,Wenjie Qu,Guanying Cao,Yanjie Zhang,Jingjie Yu
CsPbBr 3 quantum-dot borosilicate microcrystals and Eu 3+ -doped CsPbBr 3 quantum-dot microcrystals with different concentrations of Eu 3+ are successfully prepared by high temperature melting. The particle morphology of the microcrystals is characterized by scanning electron microscopy (SEM). The fluorescence characteristics are analyzed by fluorescence spectroscopy and CIE chromaticity coordinates . In this research, CsPbBr 3 quantum dots are effectively coated with borosilicate microcrystals to improve the stability of CsPbBr 3 quantum dots while ensuring its strong green emission at 517 nm. The energy transfer from CsPbBr 3 quantum dots to Eu 3+ occurs after doping. When changing the concentration of Eu 3+ , the emission peaks of perovskite broaden and blue shift occurs (517 nm→474 nm). The CIE color coordinate moves from (0.0807, 0.7200) to (0.4537, 0.2724). Therefore, the continuous adjustment of solid perovskite materials from green light to blue light and then to red light region is realized.
研究领域:
材料科学
·
纳米光学
·
无机非金属材料
·
光电子学
·
发光材料
·
固态化学
✓ 已验证
DOI
高影响因子
危险品化学品经营许可证（带存储）