CERAMICS INTERNATIONAL
·
2022
·
IF 5.532
Lulu Wang,Beiyue Ma,Xinming Ren,Chao Yu,Chengji Deng,Chunming Liu,Chuanbo Hu
In an attempt to enhance the sintering and mechanical performance of porous cordierite ceramics (Mg 2 Al 4 Si 5 O 18 ) as support materials for vehicle exhaust catalysts, ZrO 2 and M x O y (M = La, Ce, and Nb) were simultaneously introduced into cordierite sintered at 1350 °C for 4 h. Then, the reinforced function of ZrO 2 and M x O y on the properties of porous cordierite ceramics was systematically evaluated, especially for the sample co-doped with ZrO 2 and La 2 O 3 . The results displayed a distinct enhancement in mechanical and thermal performance, and the cold compressive strength increased from 72.74 to 158.59 MPa as well as thermal conductivity ranged from 1.66 to 2.01 W m −1 K −1 , respectively. It is found that ZrO 2 facilitated activation sintering introduced via lattice distortion in cordierite and La 2 O 3 accelerated the formation of cordierite and ZrSiO 4 microcrystalline through the low-temperature liquid phase. The synergic effect between ZrO 2 and La 2 O 3 , therefore, had a significant role in the reinforced mechanical and thermal performance of porous cordierite ceramics. This work not only offers a feasible strengthening strategy, but also expands the possibilities for building high-performance structural and functional ceramics .
研究领域:
材料科学
·
陶瓷工程
·
汽车工程
✓ 已验证
DOI
高影响因子
JOURNAL OF PHOTOCHEMISTRY AND PHOTOBIOLOGY A-CHEMISTRY
·
2026
·
IF 4.4
Mengchao Feng,Yuchang Wang,Xuewei Lang,Feng Wei,Huayan Si,Jianbin Zhang
This work reports the synthesis of a novel ( α / β- CdS)/Ce(OH)CO 3 composite featuring both heterojunction and heterogeneous junction structures via a simple injection titration-stirring method. The as-prepared composite exhibited excellent visible-light-driven photocatalytic activity for the degradation of high-concentration oxytetracycline (OTC) solution. Under optimal conditions determined by single-factor and response surface analyses, 0.0300 g of the composite achieved a 75.26% degradation efficiency for 50 mL of 160 mg/L OTC solution within 120 min of visible light irradiation. Notably, the composite demonstrated remarkable stability, retaining 62.39% of its initial activity after five cycles, and showed enhanced performance under real sunlight for 120 min, with a degradation rate of 78.50%. The improved photocatalytic performance is attributed to the uniform dispersion of CdS nanoparticles with abundant sulfur vacancies, which increase light absorption and facilitate charge carrier separation. Furthermore, the formation of direct Z -scheme heterojunctions and heterogeneous junctions between CdS and Ce(OH)CO 3 promotes efficient separation and transport of photogenerated carriers, thereby enhancing both photocatalytic activity and material stability.
✓ 已验证
DOI
高影响因子
SEPARATION AND PURIFICATION TECHNOLOGY
·
2023
·
IF 8.6
Dongping Zhang,Yongdi Liu,Yanyu Song,Xianbo Sun,Wen Liu,Jun Duan,Zhengqing Cai
A Fe-doped CeO 2 was fabricated for catalytic ozonation of Amoxicillin (AMX), and the catalytic mechanisms were explored in this study. Under optimal conditions (the initial solution pH of 7.0, FC-0.3 dosage of 0.5 g/L, O 3 dosage of 4 mg/min), the AMX and TOC removal by the optimal material (FC-0.3, at Fe/Ce atomic ratio of 0.3) reached 98.1 % at 24 min and 55.2 % at 36 min, respectively. Improved the AMX mineralization efficiency by 3.7 times. The experiments and theoretical calculation reveal the mechanisms of promoted catalytic ozonation by FC-0.3: 1) Highly abundant surface-active sites (i.e., –OH) enabled the adsorption of H 2 O and O 3 , which was favorable to the generation of reactive oxygen species (ROS) and improved the reaction probability for ROS and contaminants. 2) The synergistic effect between Ce 4+ /Ce 3+ and Fe 3+ /Fe 2+ redox couples accelerated the electron transfer and formation of ROS. More than 42 % of •OH was generated in the presence of FC-0.3, and the •OH, •O 2 − and 1 O 2 were the main ROS that contributed to AMX degradation. The surface OH groups played a key role in the catalytic ozonation. The oxygen vacancies (OVs) played an important role in electron transfer, Ce and Fe were the active sites of electrons transfer following the sequence of (Ce 3+ + Fe 2+ ) → (Ce 4+ + Fe 3+ ) → (Ce 3+ + Fe 2+ ) redox reaction. The degradation pathway investigation and toxicity evaluation revealed that some more toxic intermediates were generated during the ozonation process, and sufficient mineralization is required to meet safe discharge. This study provides reference for the synthesis of new catalysts and insight into the reaction mechanisms in the heterogeneous catalytic ozonation process.
✓ 已验证
产品关联
DOI
高影响因子
Advanced Energy and Sustainability Research
·
2023
·Vol. 4
·期 9
·2300023
·
IF 5.8
Shuai Zhang,Mingzi Sun,Leilei Yin,Siyuan Wang,Bolong Huang,Yaping Du,Chun-Hua Yan
The oxygen evolution reaction (OER) is critical for renewable energy conversion and storage devices. However, the rational design of electrocatalysts with suitably high efficiency and stability in strongly acidic electrolytes remains a major challenge. Herein, a solid-phase synthesis strategy is developed for the preparation of Ir-Ln (Ln = La, Ce, Pr, Nd) alloy nanoparticles with uniform particle size on carbon supports as superior acidic OER catalysts. Tailoring by the rare earth (RE) elements, Ir 2 Pr achieves a maximum mass activity of 2.10 A mg −1 Ir at 300 mV overpotential and stability over 200 h at 10 mA cm −2 in 0.5 m H 2 SO 4 , which is 9.5 and 20 times higher to pure Ir nanoparticles. Furthermore, Ir 2 Pr alloy nanoparticles exhibit excellent durability in strongly acidic electrolytes. Theoretical calculations have confirmed that the OER performances are strongly related to the RE elements in the alloy, where the d-band centers show a consistent trend with the overpotential. Moreover, the highest electroactivity of Ir 2 Pr is attributed to the improved electron transfer by 4 f orbitals and the suitable binding strength of intermediates. Herein, a fundamental understanding of the lanthanide–electrochemical performance relationship is provided and will also inspire the rational design of efficient nanoscale RE alloy electrocatalysts.
✓ 已验证
产品关联
DOI
高影响因子
MATERIALS CHEMISTRY AND PHYSICS
·
2023
·
IF 4.6
Xiao Teng,Bo Zhang,Luxia Yin,Wanyi Tao,Zhang Wen,Zekai Zhang,Wensheng Ning
A series of PdO/CeO 2 /SiO 2 -z aerogel composites with different molar ratio of Si/Ce were facilely fabricated via sol-gel method combined with atmospheric drying technology, where a major of Ce 3+ species could be oxidized to Ce 4+ species by adding hydrogen peroxide. They were used to remove thiophenics from model fuels and aromatics, compared with PdO/SiO 2 and CeO 2 /SiO 2 aerogel composites. Adding Ce and Pd led to an appearance of weak Lewis acid centers on the surface of adsorbents. Compared with PdO/SiO 2 and CeO 2 /SiO 2 , the adsorption capacity of PdO/CeO 2 /SiO 2 -z significantly increased, in which PdO/CeO 2 /SiO 2 -100 performed best and the adsorption capacity for thiophene was 15.0 mg-S/g ads , which was about the sum of PdO/SiO 2 -636 and CeO 2 /SiO 2 -100. The case was attributed to π-complexation of Pd 2+ and S-M (Pd, Ce, acted as Lewis acid centers) bond (σ) with thiophenics, where the adsorption process was dominated by S–Ce bond. Combined with the same chemical state of Pd and Ce in single metal and bimetal adsorbents verified by XPS , it can be deduced that no synergistic interaction between Pd and Ce species was formed in the adsorption process. PdO/CeO 2 /SiO 2 -100 exhibited a higher resistance for competitive adsorption of aromatics and a good solvent washing regeneration performance. The adsorption process of PdO/CeO 2 /SiO 2 -100 for thiophene was well fitted by Langmuir isothermal and pseudo-secound-order model and were spontaneous and endothermic. The solvents (n-heptane, benzene and p-xylene) have no obvious effect on the adsorption thermodynamics and kinetics of PdO/CeO 2 /SiO 2 -100.
✓ 已验证
产品关联
DOI
高影响因子
MINERALS ENGINEERING
·
2022
·
IF 5.479
Lu Xing,Xifei Ma,Kaibo Hu,Hanmeng Yuan,Jia Wei,Hongshuai Gao,Yi Nie
Since neodymium (Nd) has similar physicochemical properties to lanthanum (La), cerium (Ce) and praseodymium (Pr), their efficient separation and purification is very difficult. Three new phosphate-based ionic liquids (ILs): N,N-dimethyloctylamine bis(2-ethylhexyl)phosphate ([N 1,1,8,H ][DEHP]), N,N-dimethyldecylamine bis(2-ethylhexyl)phosphate ([N 1,1,10,H ][DEHP]), N,N-dimethyldodecylamine bis(2-ethylhexyl)phosphate ([N 1,1,12,H ][DEHP]) were synthesized and evaluated for selective separation of Nd(III) from aqueous solution. The influences concentration of Nd(III), phase volume ratio (O/A), cation chain length of ILs, extraction time, extraction temperature, salt concentration, solution acidity have on the performance of ILs for extraction separation of Nd(III) from aqueous solution were systematically investigated. It was found that the extraction efficiency ( E ) of Nd(III) using [N 1,1,8,H ][DEHP] was close to 100% at pH of 4, and that it only required 10 min to reach extraction equilibrium at 303 K. Meanwhile, the separation factors ( β ) values of β Nd/La , β Nd/Ce , β Nd/pr using [N 1,1,8,H ][DEHP] were all higher than 3. The density functional theory (DFT) results indicated that the interaction between [N 1,1,8,H ][DEHP] and Nd were stronger than that between La , Ce and Pr . In addition, almost 100% of Nd(III) could be recycled from the loaded [N 1,1,8,H ][DEHP] phase using 0.16 mol·L −1 hydrochloric acid via one step, and the E of Nd(III) by regenerated [N 1,1,8,H ][DEHP] remained about 97% after eight cycles. Moreover, the extraction mechanism of Nd(III) using [N 1,1,8,H ][DEHP] was complexation mechanism based on infrared spectroscopy and slope analysis. This work furnishes a strategy for selective separation of Nd(III) using phosphate-based ILs without diluent.
✓ 已验证
产品关联
DOI
高影响因子
MICROCHEMICAL JOURNAL
·
2023
·
IF 4.8
Xixiang Meng,Caizhi Lv,Xiaohui Wen,Xiandeng Hou,Chenghui Li,Juan He
A new bimetallic-centered MOFs, NH 2 -MIL-125(Ti/Ce), was synthesized by partially replacing Ti with Ce. The doping of Ce endowed the MOFs oxidase-like activity and enabled the construction of a ratiometric fluorescence sensing system in combination with o-phenylenediamine (OPD) for detecting trace Cu 2+ with a limit of detection of 16 nM and a linear range of 0.02–50 μM. Trace Cu 2+ was successfully quantified in real water samples. The doping of Ce also increased the photocatalytic capability of the MOFs by about 2 times, achieving excellent reduction of Cr(Ⅵ) under natural light conditions.
✓ 已验证
产品关联
DOI
高影响因子
Surfaces and Interfaces
·
2022
·
IF 6.137
Weiquan Li,Die Hu,Ke Yin,Chenglong Yu,Bichun Huang
A series of hierarchical Ru-Ce/H-ZSM-5 were designed and synthesized using the sol-gel method, and they were applied as catalysts for the catalytic combustion of chlorobenzene. The pore diameter of the catalyst was adjusted using an amount of sodium alginate (SA). Among all of the catalysts synthesized, the 0.8 wt.%Ru-10 wt.%Ce/H-ZSM-5 catalyst with a crystallization recipe of 1SiO 2 : 0.02Al 2 O 3 : 0.15TPAOH: 0.04SA: 40H 2 O (named RCZA-0.04) exhibited the optimal catalytic activity, with the 90% conversion of chlorobenzene at 247 °C. In addition, the RCZA-0.04 catalyst maintained superb stability during a long-term reaction at 325 °C. The results of characterizations demonstrated that RCZA-0.04 possessed the largest mesoporous volume, which reduced the diffusion resistance of chlorobenzene and increased the dispersion of the active components, thereby enhancing the catalytic activities. Moreover, the RCZA-0.04 catalyst possessed a low Brønsted/Lewis ratio, which was conducive to the adsorption of chlorobenzene and the cleavage of the C Cl bond.
✓ 已验证
产品关联
DOI
高影响因子
JOURNAL OF COLLOID AND INTERFACE SCIENCE
·
2022
·
IF 9.965
Kangning Wang,Mengran Qin,Chuantao Wang,Ting Yan,Yanzhong Zhen,Xiaolei Sun,Jianwei Wang,Feng Fu
The construction of composite materials is an effective strategy to solve the problems of poor conductivity, manganese dissolution, and volume expansion of manganese-based materials. Herein, a CeO 2 /MnO x @C hollow composite cathode derived from the self-assembly of Ce-Mn-metal-organic frameworks (Ce-Mn-MOFs) was synthesized. The abundant oxygen vacancies and good electronic/ionic conductivity of CeO 2 improve the electrical conductivity of composite, enhancing the rate performance. The unique hollow structure could inhibit manganese dissolution and alleviate volume expansion. The results indicate that the 1 % CeO 2 /MnO x @C composite cathode possesses a high reversible capacity and excellent cycling stability. Specifically, the 1 % CeO 2 /MnO x @C composite cathode shows a remarkable reversible specific capacity of 130 mAh/g at a current density of 500 mA g −1 , 6.5 times more than the pure MnO x (20 mAh/g). The capacity retention is up to 99.5 % relative to the initial capacity after 800 cycles. This study provides a new strategy for designing rare-earth composite electrodes to improve electrochemical performance.
✓ 已验证
产品关联
DOI
PubMed
高影响因子
Journal of Advanced Ceramics
·
2022
·Vol. 11
·期 11
·1801-1814
·
IF 11.534
Cheng Fuhao,Zhang Fengnian,Liu Yufeng,Guo Meng,Cheng Chufei,Hou Jiadong,Miao Yang,Gao Feng,Wang Xiaomin
Environmental barrier coatings (EBCs) with excellent chemical resistance and good high-temperature stability are of great significance for their applications in next-generation turbine engines. In this work, a new type of high-entropy fluorite-structured oxide (Ce 0.2 Hf 0.2 Y 0.2 Pr 0.2 Gd 0.2 )O 2− δ (HEFO-1) with different Ti 4+ contents were successfully synthesized. Minor addition of Ti 4+ could be dissolved into a high-entropy lattice to maintain the structure stable, effectively reducing the phase formation temperature and promoting the shrinkage of bulk samples. Heat treatment experiments showed that all the samples remained a single phase after annealing at 1200–1600 °C for 6 h. In addition, high-entropy (Ce 0.2 Hf 0.2 Y 0.2 Pr 0.2 Gd 0.2 Ti 0.2 x )O 2− δ demonstrated great resistance to calcium—magnesium—alumina—silicate (CMAS) thermochemical corrosion. When the content of Ti was increased to x = 0.5, the average thickness of the reaction layer was about 10.5 after being corroded at 1300 °C for 10 h. This study reveals that high-entropy (Ce 0.2 Hf 0.2 Y 0.2 Pr 0.2 Gd 0.2 Ti 0.2 x )O 2− δ is expected to be a candidate for the next-generation EBC materials with graceful resistance to CMAS corrosion.
✓ 已验证
产品关联
DOI
高影响因子
Analytical Methods
·
2022
·Vol. 14
·期 32
·3094-3102
·
IF 3.532
Linan Guo,Yahui Wang,Meng Yan,Xinxin Li,Xinyao Jiang,Manman Wang,Qian Wang,Xuesheng Wang,Yulan Hao
A cerium (Ce)-doped metal–organic framework composite (Ce/DUT-52) was prepared by using a solvothermal method and was explored as a sorbent for dispersive solid phase extraction (DSPE) of three estrogens (α-estradiol, estrone, and hexestrol) in human urine samples. After doping with Ce(III), Ce/DUT-52 exhibited more attractive features involving a higher specific surface area (774.7 m2 g−1) and zeta potential (31.4 mV), which made it an efficient adsorbent for the separation and enrichment of estrogens. The factors influencing DSPE efficiency such as the adsorbent amount, extraction time, pH, NaCl concentration, elution solvent and elution volume were investigated in detail. Under the evaluated conditions, Ce/DUT-52 showed good reusability (n = 6, RSDs ≤ 4.8%). Notably, the cofunction of electrostatic interaction, hydrophobic interaction, hydrogen bonding and π–π interaction might play major roles between estrogens and Ce/DUT-52. Finally, coupled with high-performance liquid chromatography (HPLC), a fast and sensitive method was established, which provided low limits of detection (1.5–2.0 ng mL−1), wide linear ranges (3–500 ng mL−1) and satisfactory recoveries (79.8–96.1%). The results demonstrated that Ce/DUT-52 had excellent adsorption ability to the targets and the developed method provided an alternative strategy for the determination of trace estrogens or other compounds with similar chemical structures in urine samples.
✓ 已验证
产品关联
DOI
PubMed
高影响因子
Journal of Physical Chemistry C
·
2022
·
IF 4.177
Lin Zhu,Zhen Ai,Baoli Wang,Siyue Zhang,Ruyi Zou,Yuhao Huang,Wei Sun
This paper presents an attempt on deconvoluting diffusion-control current (id) and surface-control current (is) from total current in a galvanostatic charge–discharge (GCD) test. Using this strategy, the pseudocapacitive behavior of nanosized Ce-CoO dispersed on graphene support was studied in detail. The results show that id is greatly affected by operating potential and occupies some proportion of the total pseudocapacitive current. The main functions of Ce in the composite material include promoting the proportion of is or inhibiting id and finally stimulating a specific capacitance (Cs) value increased from 192 to 726 F g–1. The Bode curve in the low-frequency region also proves that Ce can promote the performance of pseudocapacitance.
✓ 已验证
产品关联
DOI
高影响因子