ACS Applied Nano Materials
·
2018
·
IF 0
Lu Shen,Yong Li,Wenjie Zhao,Lijing Miao,Weiping Xie,Huanming Lu,Kui Wang
In order to hold the excellent corrosion resistance of zinc-rich epoxy coatings with reduced zinc content, five types of graphene modified zinc-rich epoxy coatings (G-ZRCs) were prepared. The effect of zinc content on the corrosion protection behaviors of G-ZRCs was investigated using electrochemical impedance spectroscopy (EIS). Open circuit potential (OCP) was also utilized to deepen the understanding of the anticorrosion mechanism of the as-prepared composite coatings. The results confirmed that addition of 0.3 wt % graphene could make the coating with 40 wt % (G-40ZRC) and 55 wt % zinc (G-55ZRC) provide cathodic protection for a short period of time. The EIS and OCP results showed a dominant physical barrier protection mechanism for the coatings without zinc (G-ZRC), while there was a mixed mechanism for G-40ZRC and G-55ZRC and a dominant cathodic protection mechanism for the coatings with 70 and 85 wt % zinc (G-70ZRC and G-85ZRC). Furthermore, the graphene modified zinc-rich coatings and corresponding corrosion products immersed in a 3.5% NaCl solution for 100 days were also characterized, which could further reveal anticorrosion mechanisms of the graphene modified zinc-rich coatings and the passivation effect of polyaniline (PANI).
研究领域:
材料科学
·
腐蚀与防护
✓ 已验证
产品关联
DOI
Journal of Chemistry
·
2010
·Vol. 9
·期 1
·435-442
·
IF 0
Yabin Wang,Yanni Li,Fang Wang
The protective performances of coating formed by organo-silane with a linear alkyl chain for promoting aluminum alloy corrosion protection were evaluated by electrochemical techniques. The coatings were self-assembled in the hydrolyzed hydroalcoholic bath of n -octyltriethoxysilane (OS) and cured at hot air oven by different time. The coatings prepared by the less self-assembled number and shorter cured time, were always porous and scarcely protective. On the contrary, those built by the more self-assembled number and the longer cured time had higher coverage on aluminum surface and favorable corrosion resistant property. The best results were obtained when n -octyltri-ethoxysilane (OS) was hydrolyzed 25 h, self-assembling of OS was conducted for five times and the multi-layers were cured at 120 for 1∼2 hours. In this case, the thicker, high cross-linked and more scarcely defective layer was formed on aluminum alloy surface.
研究领域:
材料科学
·
表面工程
·
腐蚀与防护
·
高分子化学
·
电化学
✓ 已验证
DOI
PROGRESS IN ORGANIC COATINGS
·
2020
·
IF 4.469
Haihua Wang,Wenjing Zhang,Yongning Ma,Guiqiang Fei,Huan Wen,Liyu Sun,Yanming Shao,Yong-Mook Kang
The compatibility between polypyrrole (PPy) and waterborne epoxy coating (EP) remains the main challenge. Here, phosphorylated poly (vinyl alcohol) (PPVA) and p-toluene sulfonic acid sodium (p-TSA) were simultaneously utilized as dopants to modify PPy and prepare water dispersible PPVA/p-TSA/PPy (PPVAT/PPy) solution. Additionally, poly (vinyl alcohol) (PVA) and TSA were also adopted to prepare PVA/p-TSA/PPy (PVAT/PPy) for comparison. Denser film with granular morphology was observed for PPVAT/PPy nanocomposite film. Compared with PVAT/PPy-40 %, the tensile strength of PPVAT-8.0 %/PPy-40 % increased from 248.8–283.9 MPa. PPVAT/PPy displayed higher compatibility and interactions with EP compared to PPy-TSA and PVAT/PPy. Compared with EP, the impedance modulus of PVAT/PPy+EP and PPVAT/PPy+EP increased from 3.17×10 5 to 1.07×10 8 and 1.62×10 9 Ω·cm 2 ; corrosion current density I corr decreased from 1.49×10 −6 to 7.72×10 -8 and 4.01×10 -9 A·cm -2 ; corrosion potential E corr displayed a positive shift of 230 mV and 269 mV, respectively. The corrosion inhibition efficiency of PPVAT/PPy+EP reached 99.83 %, which is much higher than that of PVAT/PPy+EP (93.97 %). PPVAT/PPy+EP nanocomposite coating has been proved to have preferable long-term corrosion resistance based on electrochemical impedance spectra (EIS), polarization curves and salt water spray test. The simultaneous incorporation of phosphate anions, sulfate ions and PPy into EP was beneficial to fabricate high-performance anticorrosion coating.
研究领域:
材料科学
·
高分子化学
·
腐蚀防护
·
纳米复合材料
·
表面工程
✓ 已验证
DOI
高影响因子
SURFACE & COATINGS TECHNOLOGY
·
2023
·
IF 5.4
Yang Guo,Xiaoying Guo,Haipeng Lu,Xian Jian
Developing high–efficient microwave absorbing (MA) materials with anti–corrosion (AC) properties to tackle the harsh hygrothermal marine conditions remains a challenge. Herein, we employed catalytic chemical vapor deposition and the Stöber technique to fabricate gradient multilayer interface–coupled FeNi@C@SiO 2 composites, guided by the hetero–interface engineering. The resulting composites exhibited exceptional MA properties and AC behavior. Specifically, they showcased a remarkable effective absorption bandwidth of 6.27 GHz at 1.40 mm, outperforming that of FeNi (3.80 GHz). This improved bandwidth was attributed to the electron conduction pathway provided by the C layer, which facilitated electron migration and hopping. The C@SiO 2 layer, containing defects and –OH functional groups, induced abundant dipole polarization and optimizes the impedance matching of FeNi. Furthermore, the RCS reduction value of FeNi@C@SiO 2 could reach 16.73 dB·m 2 . Moreover, the corrosion rate of FeNi@C@SiO 2 was 7.48 × 10 −11 m/s, significantly lower than that of FeNi (1.29 × 10 −10 m/s). This reduction was primarily due to the intrinsic inertness and impermeability of the C@SiO 2 layer, effectively isolating the corrosive medium from the substrate. This investigation presents a novel point of reference for the advancement of bifunctional MA materials intended to cope with extreme environments.
研究领域:
材料科学
·
纳米复合材料
·
表面工程
·
电磁功能材料
·
腐蚀防护
✓ 已验证
DOI
高影响因子
Journal of Materials Research and Technology-JMR&T
·
2022
·
IF 6.267
Xiaomeng Li,Shuxue Zhou
MXene is becoming more and more active in the field of anticorrosion coatings. In this work, Ti 3 C 2 nanosheets were modified with dopamine monomer and then introduced into waterborne epoxy coatings (EP). Composite coatings with unmodified Ti 3 C 2 nanosheets were also prepared for comparison. Anticorrosion properties of the coatings were evaluated via electrochemical impedance spectroscopy and salt spray tests in detail. Dopamine monomer was readily attached to Ti 3 C 2 nanosheets via chemical bond and saturated at 0.075 mg/mg Ti 3 C 2 . The modified Ti 3 C 2 (D-Ti 3 C 2 ) showed slightly deteriorated dispersibility in water but better dispersibility in waterborne epoxy resin relative to unmodified Ti 3 C 2 . The impedance modulus of D-Ti 3 C 2 coatings achieved four and two orders of magnitude enhancement compared with EP and unmodified Ti 3 C 2 coatings, respectively. The addition of D-Ti 3 C 2 reduced the water absorption of EP by 80% after a prolonged immersion process. Superior barrier ability and enhanced dispersion of D-Ti 3 C 2 nanosheets were responsible for the efficient enhancement of the anticorrosion performance of waterborne epoxy resin coating.
研究领域:
材料科学
·
腐蚀防护
·
纳米复合涂层
·
表面化学
✓ 已验证
DOI
高影响因子
JOURNAL OF POLYMER RESEARCH
·
2017
·Vol. 24
·期 4
·59
·
IF 1.615
Yuan Ruixia,Wu Shiqi,Wang Huaiyuan,Hu Lin,Zhu Yanji,Gao Simeng,Zhu Yixing,Zhang Xiguang
In this paper, a novel multifunctional superamphiphobic coating for anticorrosion was successfully prepared on aluminum substrate via a simple spraying technique. Al 2 O 3 nanoparticles were chemically grafted onto montmorillonite (MMT) nanosheets via coupling effect of NH 2 -C 3 H 6 -Si(OC 2 H 5 ) 3 (KH-550) and then modified by low surface energy material polydimethylsiloxane (PDMS). The ethylene tetrafluoroethylene (ETFE) composite coating with 25 wt% MMT/Al 2 O 3 -PDMS binary nanocomposite exhibited well-designed nano/μ structures and possessed superamphiphobicity with high contact angles towards water (164°), glycerol (158°) and ethylene glycol (155°). This coating demonstrated outstanding self-cleaning ability and strong adhesive ability (Grade 1 according to the GB/T 9286). The superhydrophobicity could be maintained after 8000 times abrasion or annealing treatment for 2 h under 350 °C. The coating still retained high water-repellence after immersion in 1 mol/L HCl (146°), 1 mol/L NaOH (144°) and 3.5 wt% NaCl (151°) solutions for 30 d. It should be noted that this superamphiphobic coating revealed excellent long-term corrosion protection with extremely low corrosion rate (4.3 × 10 −3 μm/year) and high protection performance (99.999%) after 30 d immersion in 3.5 wt% NaCl solutions based on electrochemical corrosion measurements. It is believed that such integrated functional coating could pave new way for self-cleaning and anticorrosion applications under corrosive/abrasive environment.
研究领域:
材料科学
·
表面工程
·
腐蚀防护
·
纳米复合材料
·
功能涂层
✓ 已验证
DOI
高影响因子